The invention discloses a method of preparing nitrogen doped oxide comprises the following steps: 100 ~ 200mL to 5 ~ 10g by adding potassium ferricyanide, stirring at the same time, to which slowly dropping 5 ~ 10g/L citric acid solution 10 ~ 30mL, dropping after adding 6 ~ 8g of manganese powder, stirring 4 ~ 5h at room temperature, aging from 24 to 48h, then removed the supernatant, distilled water and washing the solid 3 ~ 4 times, 105 drying, and then placed in a muffle furnace, in 280 ~ 400 annealed at 2 ~ 5h, which is a kind of nitrogen doped oxides of iron and manganese. The advantages of the present invention are as follows: Manganese ferricyanide is produced by reaction of potassium ferricyanide and manganese salt, because of the presence of citric acid, the particle size of manganese hexacyanoferrate can be reduced, the dispersion and the degradation efficiency can be provided, and the nitrogen doped iron manganese oxide can be formed after calcination.
【技术实现步骤摘要】
一种氮掺杂铁锰氧化物的制备方法
本专利技术涉及环境污染控制新材料领域，尤其涉及一种氮掺杂铁锰氧化物的制备方法。
技术介绍
随着科技的发展，来自工农业生产中产生的毒害有机污染物严重威胁着环境和人类的健康，寻求一种新型高效的环境治理技术具有重要的意义。光催化技术因其节能、高效、污染物降解彻底、无二次污染优点，目前已成为一种具有重要应用前景的新兴环境治理技术。近年来，新型高效的可见光光催化剂的研制成为光催化技术中的一个重要研究内容，其中具有表面等离子共振效应的光催化材料，因其独特的表面物理化学性质和高效的可见光光催化性能，成为研究的热点之一。众所周知，铁和锰是自然界中少数但属于常见的变价元素，矿物中铁的价态为+2和+3价，锰常见的价态有+2、+4、+6和+7价等，矿物中的锰多呈+3和+4价。已有研究表明，变价金属氧化物和氢氧化物的还原溶解作用，不仅对有害有毒的无机性还原剂具有良好的净化功能，而且对环境中有机性污染物具有氧化降解功能。但这种氧化性具有效率低，降解速度慢等缺点。
技术实现思路
本专利技术的目的是为克服现有技术的不足，提供一种氮掺杂铁锰氧化物的制备方法。本专利技术...
【技术保护点】
一种氮掺杂铁锰氧化物的制备方法，其特征是依次包括如下步骤：向100～200mL水中加入5～10g铁氰化钾，搅拌，同时向其中缓慢滴加5～10g/L的柠檬酸溶液10～30mL，滴加完成后，再加入6～8g氯化锰粉末，搅拌4～5h，在室温下陈化24～48h，然后去除上清液，蒸馏水洗涤固体3～4次，105℃烘干，再置于马弗炉中，在280～400℃下煅烧2～5h，即得到一种氮掺杂铁锰氧化物。
【技术特征摘要】
1.一种氮掺杂铁锰氧化物的制备方法，其特征是依次包括如下步骤：向100～200mL水中加入5～10g铁氰化钾，搅拌，同时向其中缓慢滴加5～10g/L的柠檬酸溶液10～30mL，滴加完成后，再加...
【专利技术属性】
技术研发人员：黄文艳，董平，蒋其民，薛小强，杨宏军，蒋必彪，
申请(专利权)人：常州大学，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。