The invention discloses a preparation method of a nickel doped indium phosphate photocatalyst, which comprises the following steps: in 300 500r/s speed stirring, to the ammonium phosphate solution in nickel chloride with indium chloride solution and, after dropping at the same speed stirring for 20 40min, forming a rubber body after adding 10 30mmol glycol, stirring 50 60min, finally the system of centrifugal separation, washing with distilled water 2 Solid 4, vacuum drying, preparation of nickel doped indium phosphate catalyst. The catalyst of the present invention Doped Nickel and Indium Phosphate, which is beneficial to the transition of photogenerated electrons, avoids recombination and improves the catalytic efficiency.
【技术实现步骤摘要】
一种镍掺杂磷酸铟光催化剂的制备方法
本专利技术属于水处理领域，涉及一种镍掺杂磷酸铟光催化剂的制备方法，尤其涉及一种用于处理有机废水的光催化材料及其制备方法。
技术介绍
当前，伴随工业技术的飞速发展，人类赖以生存的水资源均受到不同程度的污染，水资源污染已经成为世界各国面临的亟待解决的问题。水中的污染物，特别是有毒有机污染物的存在，不仅造成环境污染、生态破坏，而且严重危害人类健康。这些有机污染物包括多环芳烃、多氯联苯、农药、环境干扰素、染料等。在污染物降解以及能源生产领域中，半导体光催化是最有前景的方法之一。当能量大于或等于半导体禁带宽度的光子照射在光催化剂表面上时就会产生电子-空穴对的分离，这是光催化反应的最初的基本步骤。为了寻找高效的光催化剂，大量研究工作都集中在研究光催化活性的影响因素上。掺杂催化剂有利于电子跃迁，在催化剂表面形成自由基而提高催化效率。而提高光催化效果是一项无止境的工作。
技术实现思路
本专利技术的目的是为克服现有技术的不足，提供一种镍掺杂磷酸铟光催化剂的制备方法。为解决上述技术问题，本专利技术采用以下技术方案：一种镍掺杂磷酸铟光催化剂的制备方法，包...
【技术保护点】
一种镍掺杂磷酸铟光催化剂的制备方法，其特征在于，包括如下步骤：(1)在300‑500r/s的转速搅拌下，向磷酸铵溶液中同时滴加氯化铟溶液和氯化镍溶液，滴加完成后继续在300‑500r/s的转速下搅拌20‑40min；(2)形成胶体，加入10‑30mmol乙二醇，再在300‑500r/s的转速下搅拌50‑60min，最后将整个体系离心分离；(3)用蒸馏水洗涤固体2‑4次，在102‑106℃下真空烘干，即制得镍掺杂磷酸铟光催化剂。
【技术特征摘要】
1.一种镍掺杂磷酸铟光催化剂的制备方法，其特征在于，包括如下步骤：(1)在300-500r/s的转速搅拌下，向磷酸铵溶液中同时滴加氯化铟溶液和氯化镍溶液，滴加完成后继续在300-500r/s的转速下搅拌20-40min；(2)形成胶体，加入10-30mmol乙二醇，再在300-500r/s的转速下搅拌50-60min，最后将整个体系离心分离；(3)用蒸馏水洗涤固体2-4次，在102-106℃下真空烘干，即制得镍掺杂磷酸铟光催化剂。...
【专利技术属性】
技术研发人员：程昊，白大伟，郝光明，史智鹏，
申请(专利权)人：柳州若思纳米材料科技有限公司，