The invention belongs to the field of preparation of inorganic non-metallic materials, particularly relates to a method for preparing nickel pyrophosphate micron fiber, its soluble two valent nickel salt and soluble pyrophosphate in a certain proportion in alcohol / water mixed solution after mixing evenly dissolved, stirring reaction, succeeded in alcohol / water mixed solution of hydrothermal reaction, filtration, washing and drying to obtain the target product. The invention has the advantages of simple and convenient process, high purity and low product preparation cost, and the product diameter is between 20 and 200nm, and the aspect ratio is greater than 10, and the uniformity and dispersion are good. The nickel pyrophosphate fiber prepared by the invention can be widely applied in the fields of industry, electroplating, chemical industry, electronic, electrical, mechanical and building, etc..
【技术实现步骤摘要】
本专利技术属于无机非金属材料的制备
，具体地说是涉及。
技术介绍
焦磷酸镍，分子式:Ni2P2O7 ;分子量:291.330124 [g/mol];英文名称:Nickeldiphosphate; CAS No 14448-18-1。焦磷酸镍是一种重要的无机盐产品，经常用作电镀液中的络合剂，机械加工中的除锈剂。化工生产中作分散剂和乳化剂。水处理中作软水剂，锅炉除垢剂，金属离子螯合剂。在中低温化学镀镍工艺中，因其具有优良的耐蚀性和耐磨性，同时还具有稳定的非磁性、高电阻率、低温度系数及耐热等性能，而被广泛应用于计算机硬盘、磁屏蔽设备、电子工业、石油化工管道设备、汽车零部件等方面。比如中国国家知识产权局公开的03805744.1专利技术专利中，罗纳德.斯图尔特等人利用焦磷酸镍的溶液完成了非氰化物作为该工艺成分在锌或锌合金制品上形成一种附着的铜涂层的方法(参见:罗纳德?斯图尔特等，用于锌和锌合金的非氰化物铜电镀方法，03805744.1)。目前，国内外的主要生产方法如下:在室温条件下，以氢氧化镍和磷酸为原料，在水溶液中直接沉淀得到中间产物。然后加热煅烧后...
【技术保护点】
一种焦磷酸镍微米纤维的制备方法的制备方法，其特征在于:将可溶性二价镍盐和可溶性焦磷酸盐在醇/水混合溶液中均匀溶解，搅拌反应后，接续在醇/水混合溶液中进行水热反应，过虑、洗涤、干燥即得目的产物。
【技术特征摘要】
1.一种焦磷酸镍微米纤维的制备方法的制备方法，其特征在于:将可溶性二价镍盐和可溶性焦磷酸盐在醇/水混合溶液中均匀溶解，搅拌反应后，接续在醇/水混合溶液中进行水热反应，过虑、洗涤、干燥即得目的产物。2.根据权利要求1所述的一种焦磷酸镍微米纤维的制备方法，其特征在于:所述可溶性二价镍盐为氯化镍、硫酸镍、硝酸镍或乙酸镍中的一种或两种以上的混合物。3.根据权利要求2所述的一种焦磷酸镍微米纤维的制备方法，其特征在于:所述可溶性焦磷酸盐为焦磷酸钠或焦磷酸钾中的一种或其混合物。4.根据权利要求3所述的一种焦磷酸镍微米纤维的制备方法，其特征在于:所述醇/水混合溶液中的醇为甲醇、乙醇、乙二醇、正丙醇、异丙醇...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。