The invention discloses a high hardness wear-resistant composite roll, including high hardness and high hardness of the body surface of the body with a plurality of cast wear resistant alloy block, the wear-resistant alloy block comprises the following components: the mass fraction of Si 32% accounted for 24, Zn accounted for 3.6 4.8%, Ni accounted for 2.8 of the 3.6% Ti, accounting for 1.2 2%, Mn accounted for 11.2 12%, Cr accounted for 11.2 12%, the remainder is Fe; the hardness of body by KmTBCr26 and ZGMn13Cr2 both high temperature melting, calculated according to the weight percentage, the content of KmTBCr26 accounted for 52 of the 64%, the content of ZGMn13Cr2 accounted for 36 of the 48%,. This way, the invention can have the characteristics of high hardness, high wear resistance, greatly improves the service life.
【技术实现步骤摘要】
一种高硬度耐磨型复合轧辊
本专利技术涉及一种轧辊，特别涉及一种高硬度耐磨型复合轧辊。
技术介绍
轧辊是轧钢生产中大量消耗的重要部件，轧辊质量的好坏不仅影响着轧材的表面质量，而且还影响着轧机的作业率，而且现阶段，轧辊在使用的过程中，耐磨受损极大，因此对于其自身的耐磨性能要求极高，传统的轧辊的物理性能逐渐满足不了生产使用的要求，并且轧辊在使用的过程中，与其它物体碰撞也是必不可少的一个环节，因此对轧辊的硬度要求也势必将提高。
技术实现思路
本专利技术主要解决的技术问题是提供一种高硬度耐磨型复合轧辊，能够具备有高硬度、高耐磨的特点，大幅提高使用寿命。为解决上述技术问题，本专利技术采用的一个技术方案是：提供一种高硬度耐磨型复合轧辊，包括高硬度本体，所述高硬度本体表面镶铸有多个耐磨合金块，所述耐磨合金块包括如下质量百分比含量的组分：Si占24-32%，Zn占3.6-4.8%，Ni占2.8-3.6%，Ti占1.2-2.0%，Mn占11.2-12.0%，Cr占11.2-12.0%，余量为Fe；所述高硬度本体由KmTBCr26和ZGMn13Cr2两者高温熔融而成，按照质量百分比计算，所...
【技术保护点】
一种高硬度耐磨型复合轧辊，其特征在于，包括高硬度本体，所述高硬度本体表面镶铸有多个耐磨合金块，所述耐磨合金块包括如下质量百分比含量的组分：Si占24‑32%，Zn占3.6‑4.8%，Ni占2.8‑3.6%，Ti占1.2‑2.0%，Mn占11.2‑12.0%，Cr占11.2‑12.0%，余量为Fe；所述高硬度本体由KmTBCr26和ZGMn13Cr2两者高温熔融而成，按照质量百分比计算，所述KmTBCr26的含量占52‑64%，所述ZGMn13Cr2的含量占36‑48%。
【技术特征摘要】
1.一种高硬度耐磨型复合轧辊，其特征在于，包括高硬度本体，所述高硬度本体表面镶铸有多个耐磨合金块，所述耐磨合金块包括如下质量百分比含量的组分：Si占24-32%，Zn占3.6-4.8%，Ni占2.8-3.6%，Ti占1.2-2.0%，Mn占11.2-12.0%，Cr占11.2-12.0%，余量为Fe；所述高硬度本体由KmTBCr26和ZGMn13Cr2两者高温熔融而成，按照质量百分比计算，所述KmTBCr26的含量占52-64%，所述...
【专利技术属性】
技术研发人员：王文其，
申请(专利权)人：太仓市钧胜轧辊有限公司，
类型：发明
国别省市：江苏,32