The invention relates to a method for removal of carbonate silver cyanide bath, including a, determination of carbonate content: cyanide silver plating bath, the analysis to determine the content of carbonate; B, determine the amount of precipitating agent according to the carbonate content of cyanide silver plating bath, calculation and preparing to need to add carbonate precipitation agent; C and carbonate precipitation: carbonate precipitation agent is added to the silver cyanide bath, stirring, standing, sedimentation, filtration, the filtrate is obtained. The present invention has the advantages of high removal efficiency of carbonate, short reaction time, complete reaction and little safety hidden trouble in cyanide silver plating tank liquid.
【技术实现步骤摘要】
一种去除氰化镀银槽液中碳酸盐的方法
本专利技术涉及表面工程
，具体涉及一种去除氰化镀银槽液中碳酸盐的方法。
技术介绍
氰化镀银槽液有氰化钠镀银槽液和氰化钾镀银槽液两种类型，氰化钠镀银槽液主要成份包括：银、氰化钠、碳酸钠；氰化钾镀银槽液主要成份包括：银、氰化钠、碳酸钾。碳酸盐是氰化镀银槽液成份之一，其主要作用是增加溶液的导电性，一般以Na2CO3.10H2O和K2CO3的形式存在，通常要求K2CO3含量不超过50g/L；Na2CO3.10H2O含量不超过70g/L)，在实际工作中，氰化镀银槽中碳酸盐的含量随着使用时间的增加而不断升高，这是由于氰化物的水解和从空气中吸收二氧化碳而逐渐积累的。如不采取有效控制措施，有时镀银槽碳酸盐含量会超出规定上限数倍，对镀银层质量带来较大的不利影响。采用重新配制槽液的方法可将碳酸盐含量控制在规范围内，但这将大大增加电镀成本，同时大大增加废水处理压力。现有技术是采用冷冻的方法去除部份碳酸，即利用冬季气温较低，碳酸盐随温度下降溶解度下降，从而从槽液中析出结晶，再通过过滤槽液的方法去除部份碳酸，由于碳酸盐的溶解度较高，如K2CO3在0...
【技术保护点】
一种去除氰化镀银槽液中碳酸盐的方法，其特征在于，包括：a、确定碳酸盐含量：取氰化镀银槽液，分析确定其中碳酸盐含量；b、确定沉淀剂加入量：根据氰化镀银槽液中的碳酸盐含量，计算并准备需要加入的碳酸盐沉淀剂；c、碳酸盐沉淀：将碳酸盐沉淀剂加入到氰化镀银槽液中，搅拌，静置、沉淀，过滤，取滤液，即得。
【技术特征摘要】
1.一种去除氰化镀银槽液中碳酸盐的方法，其特征在于，包括：a、确定碳酸盐含量：取氰化镀银槽液，分析确定其中碳酸盐含量；b、确定沉淀剂加入量：根据氰化镀银槽液中的碳酸盐含量，计算并准备需要加入的碳酸盐沉淀剂；c、碳酸盐沉淀：将碳酸盐沉淀剂加入到氰化镀银槽液中，搅拌，静置、沉淀，过滤，取滤液，即得。2.根据权利要求1所述一种去除氰化镀银槽液中碳酸盐的方法，其特征在于，所述碳酸盐沉淀剂为CaCl2、BaCl2、MgCl2中的至少一种。3.根据权利要求2所述一种去除氰化镀银槽液中碳酸盐的方法，其特征在于，所述碳酸盐沉淀剂为CaCl2。4.根据权利要求3所述一种去除氰化镀银槽液中碳酸盐的方法，其特征在于，包括如下步骤：Ⅰ、碳酸盐含量的确定：取氰化镀银槽液，分析确定其中碳酸盐含量；Ⅱ、确定CaCl2加入量：根...
【专利技术属性】
技术研发人员：唐恩军，郑付华，喻善远，李洁，刘智，赵云强，段睿，
申请(专利权)人：中国人民解放军第五七一九工厂，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。