Using carburizing agent an alloy steel casting, prepared from the following raw materials: Petroleum Coke 6 8 copies, 7 copies, 5 purified graphite 2 semi graphite 4, modified asphalt 1 3 copies, 5 copies, 3 silica powder 2 4 copies, 4 copies, 2 bonded silica sol 6 8 copies, 3 copies, 1 Pro flux powdered coal of 6 8 copies, 8 copies, 6 water glass ammonium bicarbonate 1 3. The invention has the advantages that the invention has the advantages of novel design, reasonable formula, process specification scientific processing, the actual use of carburetant after preparation of superior performance, ensure raw material smelting, less raw material preparation of high-quality castings, the effect is significant, and easy to use.
【技术实现步骤摘要】
一种合金钢精铸件铸造用增碳剂及其制备工艺
本专利技术涉及精密铸造
，具体涉及一种合金钢精铸件铸造用增碳剂及其制备工艺。
技术介绍
铸造是人类掌握比较早的一种金属热加工工艺，已有约6000年的历史。中国约在公元前1700～前1000年之间已进入青铜铸件的全盛期，工艺上已达到相当高的水平。铸造是将液体金属浇铸到与零件形状相适应的铸造空腔中，待其冷却凝固后，以获得零件或毛坯的方法。铸造在进行时，通过制蜡模、蜡型焊接、脱蜡、焙烧、熔炼、浇注、清理及后处理加工完成，在铸造中，其中任意一环节的规范操作，均为制备后续高品质精铸件的根本，其中熔炼阶段最为关键，其是保证金属材料的液化根本，通常都是在熔炉中进行的，精铸件通常均是采用合金钢制备而成，由于熔炼中，而在铸造件进行实际的合金钢水熔炼时，通常是使用增碳剂，这样在使用时就可以可大幅度增加废钢用量，减少生铁用量或不用生铁，但是在现有技术中，由于增碳剂实际配方配比不够合理，因此实际的使用效果并不明显，并且实际的增碳剂在实际的加工中，会涉及到大量的碳流失，直接造成能源的损失。
技术实现思路
：本专利技术所要解决的技术问题在于提供一种...
【技术保护点】
一种合金钢精铸件铸造用增碳剂，其特征在于，由以下原料制成：石油焦6‑8份、纯化石墨5‑7份、半石墨2‑4份、改性沥青1‑3份、二氧化硅3‑5份、铝粉2‑4份、结合剂2‑4份、硅溶胶6‑8份、促熔剂1‑3份、粉状精煤6‑8份、水玻璃6‑8份、碳酸氢铵1‑3份。
【技术特征摘要】
1.一种合金钢精铸件铸造用增碳剂，其特征在于，由以下原料制成：石油焦6-8份、纯化石墨5-7份、半石墨2-4份、改性沥青1-3份、二氧化硅3-5份、铝粉2-4份、结合剂2-4份、硅溶胶6-8份、促熔剂1-3份、粉状精煤6-8份、水玻璃6-8份、碳酸氢铵1-3份。2.根据权利要求所述的一种合金钢精铸件铸造用增碳剂，其特征在于，各原料的优选分量为：石油焦7份、纯化石墨6份、半石墨3份、改性沥青2份、二氧化硅4份、铝粉3份、结合剂3份、硅溶胶7份、促熔剂2份、粉状精煤7份、水玻璃7份、碳酸氢铵2份。3.根据权利要求所述的一种合金钢精铸件铸造用增碳剂，其特征在于：所述的改性沥青包括包括下述原料：沥青130份、...
【专利技术属性】
技术研发人员：焦培峰，徐大兵，徐乐高，
申请(专利权)人：天长市兴宇铸造有限公司，
类型：发明
国别省市：安徽,34