一种高分散贵金属催化剂在电化学析氢反应中的应用制造技术
A highly dispersed noble metal catalyst in the electrochemical hydrogen evolution reaction application
The invention discloses a high dispersion of the noble metal catalyst in the electrochemical hydrogen evolution reaction in the application, which is characterized in that the preparation process of the high dispersion of noble metal catalysts for carbohydrates as raw material, in the presence of transition of noble metal salt, and the soft template physical mixing, then, in an inert atmosphere in the first 400 to 650 DEG C temperature 0.5 ~ 2H, and then heated to 700 to 1200 8C 2 ~ 12h, the highly dispersed noble metal catalyst; soft template for the melamine, two cyanogen amine, two urea or single cyanide. The catalyst exhibited excellent catalytic activity and stability over a wide range of pH, especially at low temperatures. The catalyst exhibited excellent hydrogen production performance.
【技术实现步骤摘要】
一种高分散贵金属催化剂在电化学析氢反应中的应用
本专利技术属于炭材料的制备领域，具体涉及一种高分散贵金属催化剂在电化学析氢反应中的应用。
技术介绍
能源是经济发展和社会进步的重要物质基础。近年来，严峻的能源压力和环境污染问题威胁生态平衡，制约社会经济的可持续发展，成为各国关注的焦点问题。氢气是一种理想的绿色能源载体，具有无可比拟的潜在开发价值。电解水产氢是一种高效的产氢技术，具有原料来源广泛，绿色环境友好的优点。目前，Pt基催化剂仍然是电解水反应的理想催化剂。但是金属Pt在自然界中相对匮乏，成本昂贵，限制了其广泛应用。炭材料由于其高的化学稳定性，高的比表面积，卓越的机械性能以及良好的电学性质而被广泛地应用于多相催化，分离科学，能源转化等方面。为了降低生产成本，将活性金属与炭纳米材料杂化是降低金属用量，提高催化剂活性和稳定性的有效方法。复合材料一方面降低了贵金属前驱体的用量，另一方面在炭基底的牟定作用下部分地改善了催化剂的稳定性。然而，复合材料的制备过程复杂，步骤繁多，金属前驱体的还原通常需要使用过量的强还原剂。此外，热解法制备复合材料时，贵金属颗粒的尺寸难以控制，...
【技术保护点】
一种高分散贵金属催化剂在电化学析氢反应中的应用，其特征在于，所述高分散贵金属催化剂的制备过程为：以碳水化合物为原料，在过渡贵金属盐存在下，与软模板剂物理混合均匀，然后，在惰性气氛中，先在400～650℃下保温0.5～2h，再升温至700～1200℃煅烧2～12h，得到高分散贵金属催化剂；所述的软模板剂为三聚氰胺、二氰二胺、尿素或单氰。
【技术特征摘要】
1.一种高分散贵金属催化剂在电化学析氢反应中的应用，其特征在于，所述高分散贵金属催化剂的制备过程为：以碳水化合物为原料，在过渡贵金属盐存在下，与软模板剂物理混合均匀，然后，在惰性气氛中，先在400～650℃下保温0.5～2h，再升温至700～1200℃煅烧2～12h，得到高分散贵金属催化剂；所述的软模板剂为三聚氰胺、二氰二胺、尿素或单氰。2.如权利要求1所述的高分散贵金属催化剂在电化学析氢反应中的应用，其特征在于，所述碳水化合物为糖类。3.如权利要求2所述的高分散贵金属催化剂在电化学析氢反应中的应用，其特征在于，所述碳水化合物为果糖、葡萄糖或氨基葡萄糖盐酸盐。4.如权利要求1任一所述的高分散贵金属催化剂在电化学析氢反...