一种从盐酸浸淋体系萃取精制铁盐的工艺方法技术

本发明专利技术公开了一种从盐酸浸淋体系萃取精制铁盐的工艺方法，该方法包括以下步骤：1)向含有二价铁盐的溶液中滴加氧化剂溶液，使二价铁离子被完全氧化，得到含有三价铁盐的水相；2)配制萃取剂有机相；3)将步骤1)得到的水相与步骤2)得到的有机相混合，进行萃取，分离有机相：4)将步骤3)所得到的有机相使用反萃取剂进行反萃取，分相后，收集反萃取液。

Process for extracting refined iron salt from hydrochloric acid leaching system

The invention discloses a process with refined iron from hydrochloric acid leaching extraction system, the method comprises the following steps: 1) to a solution containing two ferric salt in adding oxidant solution, so that the two valent iron ions are completely oxidized, from aqueous phase containing ferric; 2) preparation of extractant in organic phase; 3) in step 1) and the 2 steps to get the water) was obtained in the organic phase mixing, extraction, separation of the organic phase: 4) step 3) obtained by using the organic phase stripping agent after separation, extraction, reverse extraction liquid collection.

【技术实现步骤摘要】
一种从盐酸浸淋体系萃取精制铁盐的工艺方法
本专利技术属于化学萃取提纯
，具体涉及一种从盐酸浸淋体系萃取精制铁盐的工艺方法。
技术介绍
应用于高铝粉煤灰、赤泥及其他含铁金属废物的资源化利用，涵盖对象包括高铝粉煤灰、赤泥、含铁金属废物及品位低于高炉冶炼要求的铁矿石。根据统计，我国堆积的高铝粉煤灰达到三亿吨，而蕴藏量达到50亿吨。高铝粉煤灰中三氧化二铝含量在35％～55％之间，按此计算，我国高铝粉煤灰中氧化铝的总含量在17.5～27.5亿吨之间。如果将这些氧化铝利用起来，按目前我国每年的氧化铝需求量(平均每年消耗氧化铝4000万吨)估计，可以满足我国125年所需，由此可以大大减少铝土矿对外依存并可避免国内因开采铝土矿而带来的环境和生态破坏。从粉煤灰中提取氧化铝，有碱法和酸法两种工艺。碱法比较直接，产品纯度高。但因大量消耗石灰石，在固体废物利用的同时，带来另外一种环境和生态的破坏，也拉高了单位产品的生产成本。和碱法相比较，酸法流程短，成本相对较低。但因为酸浸出法固有的特点，浸出液中除了氧化铝以外，其他金属，如金属铁，价值高昂的稀有金属镓以及粉煤灰中所含的其他重金属铜、锌、铅、汞等都被浸本文档来自技高网...

【技术保护点】
一种从盐酸浸淋体系萃取精制铁盐的工艺方法，其特征在于，包括以下步骤：1)向含有二价铁盐的溶液中滴加氧化剂溶液，使二价铁离子被完全氧化，得到含有三价铁盐的水相；2)配制萃取剂有机相；3)将步骤1)得到的水相与步骤2)得到的有机相混合，进行萃取，分离有机相：4)将步骤3)所得到的有机相使用反萃取剂进行反萃取，分相后，收集反萃取液。

【技术特征摘要】
1.一种从盐酸浸淋体系萃取精制铁盐的工艺方法，其特征在于，包括以下步骤：1)向含有二价铁盐的溶液中滴加氧化剂溶液，使二价铁离子被完全氧化，得到含有三价铁盐的水相；2)配制萃取剂有机相；3)将步骤1)得到的水相与步骤2)得到的有机相混合，进行萃取，分离有机相：4)将步骤3)所得到的有机相使用反萃取剂进行反萃取，分相后，收集反萃取液。2.根据权利要求1所述方法，其特征在于，所述步骤1)中的氧化剂溶液是氯酸钠溶液。3.根据权利要求1所述方法，其特征在于，所述步骤1)中的氧化剂溶液是双氧水、次氯酸钠、氯气或过硫酸铵。4.根据权利要求1所述方法，其特征在于，所述步骤1)中的萃取剂有机相组成如下(体积％)：甲基异丁酮：15～35％磷酸三丁酯：35～70％正辛...

【专利技术属性】
技术研发人员：王毅，王邦达，孙应龙，
申请(专利权)人：清华大学，
类型：发明
国别省市：北京,11