The invention discloses a nano sand fixing binder and its application. The preparation process of the binder of the invention is: the attapulgite water, according to the mass ratio (1~2): 10 mixed, attapulgite after immersed in water for 20h~28h, stirring, until crushed into a uniform suspension, diluted with water to obtain the nanometer sand binder, the binder can be used in nano sand windbreak areas. The material used in the invention is a natural material, stable property, will bring two pollution, wide material source, low cost, simple preparation process, easy to use and operation of large area; the invention can improve the soil properties of sand binder, enhance soil water holding capacity, promote the growth and reproduction of natural plant settled that can speed up the process of ecological restoration and fixed sandy land.
【技术实现步骤摘要】
一种环保型纳米固沙粘结剂及其制备方法与应用
本专利技术属于环保材料领域，尤其涉及一种环保型纳米固沙粘结剂及其制备方法与应用。
技术介绍
现有的技术多是采用高分子有机化合物作为粘结剂的主要成分，虽然粘结性和固沙效果尚可，但不环保、成本高，大面积喷洒高分子有机化合物具有潜在的环境风险。
技术实现思路
本专利技术的目的在于提供一种环保型纳米固沙粘结剂及其制备方法与应用，旨在解决上述
技术介绍
中的不足。本专利技术是这样实现的，一种纳米固沙粘结剂，该粘结剂的制备过程为：将凹凸棒石、水按质量比（1~2）：10混合，凹凸棒石在水中浸泡20h~28h后，搅拌、捣碎直至成均匀悬浊液，加水稀释后得到纳米固沙粘结剂。优选地，所述凹凸棒石、水按质量比1：10混合。优选地，所述纳米固沙粘结剂中凹凸棒石和水的质量比为1：（100~200）。本专利技术进一步公开了上述纳米固沙粘结剂在防风固沙方面的应用。将纳米固沙粘结剂用喷雾、喷洒设备在流动沙地表面进行喷洒，经自然干燥后，凹凸棒纳米粒子将松散的沙粒胶结起来，在沙地表层形成一个具有较强抗风蚀能力的稳定层，起到防风固沙作用。相比于现有技术的缺点和不足，本专利技术具有以下有益效果：（1）本专利技术所用材料为天然材料，性质稳定，不会带来二次污染，材料来源广泛，费用低廉，制备工艺简单，易于操作和大面积推广使用；（2）本专利技术固沙粘结剂的使用能改良土壤性质，增强沙土的保水能力，促进天然植物的定居和生长繁殖，能加速沙地固定和生态恢复进程。具体实施方式为了使本专利技术的目的、技术方案及优点更加清楚明白，以下结合实施例，对本专利技术进行进一步详细说明。应当理...
【技术保护点】
一种纳米固沙粘结剂，其特征在于，该粘结剂的制备过程为：将凹凸棒石、水按质量比（1~2）：10混合，凹凸棒石在水中浸泡20h~28h后，搅拌、捣碎直至成均匀悬浊液，加水稀释后得到纳米固沙粘结剂。
【技术特征摘要】
1.一种纳米固沙粘结剂，其特征在于，该粘结剂的制备过程为：将凹凸棒石、水按质量比（1~2）：10混合，凹凸棒石在水中浸泡20h~28h后，搅拌、捣碎直至成均匀悬浊液，加水稀释后得到纳米固沙粘结剂。2.如权利要求1所述的纳米固沙粘结剂...
【专利技术属性】
技术研发人员：张彦，何学良，赵赏鑫，张贵赞，周永涛，李佳萌，姚瑶，陈吉祥，刘左军，张继义，
申请(专利权)人：中石油北京天然气管道有限公司，兰州理工大学，
类型：发明