The present invention provides a method for preparing antistatic agent with polyether modified silicone oil, which is characterized in that the preparation method comprises the following steps: according to the weight, polyether 100, hydrogen containing silicone oil 80 180 copies, 5 copies of 1 chloroplatinic acid, 10 30 isopropyl alcohol, in nitrogen environment, 2 6h 80 reaction at a temperature of 110 DEG C, the product obtained by filtration, separation, crude polyether modified silicone products, the polyether modified silicone oil crude product pass into the column is provided with an efficient adsorbent, the flow rate of 0.5BV, high purity polyether modified silicone oil product is obtained.
【技术实现步骤摘要】
一种制抗静电剂用聚醚改性硅油的制备方法
本专利技术涉及一种聚醚改性硅油的制备方法，尤其是一种制抗静电剂用聚醚改性硅油的制备方法。
技术介绍
聚醚改性硅油是一种性能独特的有机硅非离子表面活性剂。其具有良好的润滑性，更低的表面张力，更好的柔软特性及抗静电性能，良好的流平性，可很好地改善树脂的分子间的应力，克服这些树脂本身的缺点，获取新的性能，它具有较好的破乳性，适用于某些特定场合的油水分离，本产品与聚二甲基硅氧烷相比，可以任意比例与水互溶，也与极性有机溶剂如醇、DMF、醚、酯等互溶，与甲苯、烷烃等非极性溶剂部分或完全相溶。使用方便，应用领域广泛。CN105504289A公开了一种聚醚改性硅油的制备方法，包括：在多孔陶瓷负载铂催化剂的作用下，将末端烯基的聚醚与含氢硅油在溶剂中进行硅氢加成反应，过滤，收集滤液；将所述滤液除去溶剂，得到聚醚改性硅油。CN105435490A公开了一种聚醚硅油石蜡消泡剂，包括以下重量百分比的组分：20～40％的聚醚、20～35％的二甲基硅油、10～25％的水、10～15％的炭黑和10～15％的石蜡。同时，本专利技术还公开了上述消泡剂的制备方法...
【技术保护点】
一种制抗静电剂用聚醚改性硅油的制备方法，其特征在于制备方法包括以下步骤：按重量份计，将聚醚100份，含氢硅油80‑180份，1‑5份氯铂酸，10‑30份异丙醇，在氮气环境，80‑110℃温度下反应2‑6h，产物经过滤，分离，得到聚醚改性硅油粗产品，将聚醚改性硅油粗产品通入装有高效吸附剂的层析柱中，流速0.5BV，即得到高纯度聚醚改性硅油产品。
【技术特征摘要】
1.一种制抗静电剂用聚醚改性硅油的制备方法，其特征在于制备方法包括以下步骤：按重量份计，将聚醚100份，含氢硅油80-180份，1-5份氯铂酸，10-30份异丙醇，在氮气环境，80-110℃温度下反应2-6h，产物经过滤，分离，得到聚醚改性硅油粗产品，将聚醚改性硅油粗产品通入装有高效吸附剂的层析柱中，流速0.5BV，即得到高纯度聚醚改性硅油产品。2.根据权利要求1所述的一种制抗静电剂用聚醚改性硅油的制备方法，其特征在于所述高效吸附剂的制备方法包括以下步骤：按重量份计，将琼脂糖疏水作用介质100份，3-氧代氮杂环丁-1-羧酸叔丁酯0.1-1份，(R)-(+)...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。