一种二维TiO2超薄纳米片及其制备方法技术

本发明专利技术公开了一种二维TiO2超薄纳米片及其制备方法。该方法是以钛酸四正丁酯以及氢氟酸作为主要原料，乙二醇作为修饰剂，通过调配各项原料物质的量，并采用高温高压下的水热法实现对超薄TiO2纳米片的合成。此种制备方法获得的TiO2纳米片分散性好，可实现片厚度约为2nm‑20nm的调控，横向尺寸约为200nm，且具有优良的光催化产氢性能，在众多领域具有潜在应用。

A two dimensional TiO2 ultrathin nanosheets and its preparation method

The invention discloses a two-dimensional TiO2 ultrathin nanometer slice and a preparation method thereof. This method is based on butyl titanate four and hydrofluoric acid as the main raw material, ethylene glycol as a modifier, through the allocation of the amount of raw material, and by hydrothermal method under high temperature and high pressure synthesis of ultrathin TiO2 nanosheets. The preparation method of the nano TiO2 dispersion, can realize the film thickness of about 2nm regulation 20nm, transverse size is about 200nm, and has excellent photocatalytic performance, has potential applications in many fields.

【技术实现步骤摘要】
一种二维TiO2超薄纳米片及其制备方法
本专利技术属于无机非金属及光催化材料制备领域，涉及一种二维TiO2超薄纳米片及其制备方法。
技术介绍
TiO2作为最重要的氧化物半导体之一，已经被广泛的研究并且在能源和环境领域得到了很多应用。其中，光降解有机染料、光分解水制氢等光催化性能与TiO2的暴露晶面密切相关。其中锐钛矿TiO2中(001)和(101)晶面在选择性分离光生载流子中起到了重要作用，这对光催化的影响是很大的。现阶段为了制备高(001)晶面暴露率的TiO2所面临的问题可分为两个方面：一是不规则形貌问题，另一个是纳米片聚集问题。在本专利技术的制备方法中引入乙二醇作为修饰剂，期望通过HF和乙二醇的协同作用，使得(001)晶面的暴露率提高的同时，增强其分散性，从而提高其光催化性能。
技术实现思路
本专利技术的目的在于针对现有技术的不足，提供一种二维TiO2超薄纳米片及其制备方法，该方法采用水热法实现二维TiO2超薄纳米片的合成，获得的TiO2纳米片厚度范围约为2～20nm，横向尺寸约为200nm，(001)面暴露率约为97％，分散性好，产氢速率最高达到19.24mmolh-1g-1，根据本文档来自技高网...

【技术保护点】
二维TiO2超薄纳米片的制备方法，其特征是，包括以下步骤：将TBOT(钛酸四正丁酯)和HF混合，加入乙二醇，室温搅拌混合均匀；在180℃的条件下水热反应16h；所得产物用去离子水和无水乙醇清洗后，置于烘箱中烘干，获得二维TiO2超薄纳米片。

【技术特征摘要】
1.二维TiO2超薄纳米片的制备方法，其特征是，包括以下步骤：将TBOT(钛酸四正丁酯)和HF混合，加入乙二醇，室温搅拌混合均匀；在180℃的条件下水热反应16h；所得产物用去离子水和无水乙醇清洗后，置于烘箱中烘干，获得二维TiO2超薄纳米片。2.根据权利要求1所述的二维TiO2超薄纳米片的制备方法，其特征是，所述的TBOT和HF的摩尔比为...

【专利技术属性】
技术研发人员：任召辉，陈颖，阮罗渊，李铭，韩高荣，
申请(专利权)人：浙江大学，
类型：发明
国别省市：浙江,33