一种注塑模具一次裁切成型工艺制造技术

本发明专利技术公开了一种注塑模具一次裁切成型工艺，包括如下内容：a：将嵌件通过装配卡夹安装在裁切下模上，裁切上模下压合模后通过冲子裁断嵌件；b：裁断后的嵌件置于刀口上，在油缸的驱动下带动成型块向下运动，使得嵌件被折弯，并在折弯过后向上运动预留有注塑成型空间；c:经过裁切和折弯后的嵌件进行一次注塑成型后即可得到产品。本发明专利技术采用一次裁切注塑成型的方式得到复杂嵌件，生产工艺简单，而且有效避免因折弯度不满或者过度而影响产品质量，产业化成本低。

One time cutting forming process of injection mould

The invention discloses an injection mold of a cutting forming process includes the following contents: A: insert the assembly clip mounted on the cutting die, cutting on the die clamping by punch cutting inserts; B: insert a knife after cutting, drives the forming block downward movement in cylinder drive, the insert is bent, and the bending after the upward movement of reserved space through injection molding; c: insert cutting and bending after a product is obtained after injection molding. The invention adopts a cutting molding way of complex block, simple production process, and effectively avoid the bending deflection of dissatisfaction or excessive and affect the quality of products, low cost industrialization.

【技术实现步骤摘要】
一种注塑模具一次裁切成型工艺
本专利技术涉及注塑模具
，尤其涉及一种注塑模具一次裁切成型工艺。
技术介绍
在很多塑件中，为了提高塑件的强度、硬度、耐磨性等，或者是增加塑件的尺寸、便于连接安装等，一般会在塑件中镶入嵌件，通常为金属嵌件，但是嵌件的注塑产品一般需要通过二次注塑成型，尤其是复杂嵌件，这就会导致注塑工艺复杂，设备成本高。因此，为了解决上述存在的技术问题，本专利技术提供了一种新的技术。
技术实现思路
本专利技术的目的是提供了一种注塑模具一次裁切成型工艺。本专利技术针对上述技术缺陷所采用的技术方案是：一种注塑模具一次裁切成型工艺，包括如下内容：a：将嵌件通过装配卡夹安装在裁切下模上，裁切上模下压合模后通过冲子裁断嵌件；b：裁断后的嵌件置于刀口上，在油缸的驱动下带动成型块向下运动，使得嵌件被折弯，并在折弯过后向上运动预留有注塑成型空间；c:经过裁切和折弯后的嵌件进行一次注塑成型后即可得到产品。进一步地，注塑模具上配置折弯度监测装置自动监测嵌件的折弯程度。进一步地，步骤b中所述成型块的折弯操作至少一次。进一步地，成型块的折弯操作为2次。本专利技术的有益效果是：本专利技术采用一次裁切本文档来自技高网...

【技术保护点】
一种注塑模具一次裁切成型工艺，其特征在于：包括如下内容：a：将嵌件通过装配卡夹安装在裁切下模上，裁切上模下压合模后通过冲子裁断嵌件；b：裁断后的嵌件置于刀口上，在油缸的驱动下带动成型块向下运动，使得嵌件被折弯，并在折弯过后向上运动预留有注塑成型空间；c:经过裁切和折弯后的嵌件进行一次注塑成型后即可得到产品。

【技术特征摘要】
1.一种注塑模具一次裁切成型工艺，其特征在于：包括如下内容：a：将嵌件通过装配卡夹安装在裁切下模上，裁切上模下压合模后通过冲子裁断嵌件；b：裁断后的嵌件置于刀口上，在油缸的驱动下带动成型块向下运动，使得嵌件被折弯，并在折弯过后向上运动预留有注塑成型空间；c:经过裁切和折弯后的嵌件进行一次注塑成型后即可得到产...

【专利技术属性】
技术研发人员：封杨，沈晔，
申请(专利权)人：苏州菱慧电子科技有限公司，
类型：发明
国别省市：江苏,32