The invention provides a ABS plastic spraying process, which comprises the following steps: (1) the ABS annealing, the plastic is heated to 60 degrees Celsius hot deformation, thermal insulation 1.5 2H; (2) removing oil, use the cleaning agent, and then finally clean with water, dried or dried; (3) in addition to electricity and dust, using high-pressure ionized air flow except electricity and dust; (4) coating, plastic coating thickness is 15~20 m, spraying 2~3 times, each spray dried 10 15min; (5) drying, coating after 50 under 60 DEG C for 25 35min. The ABS plastic spraying process of the invention greatly reduces the cracking, foaming and falling off of the plastic coating through the control of the technological process and the parameter thereof, thereby prolonging the service life of the plastic product.
【技术实现步骤摘要】
一种ABS塑料喷涂工艺
本专利技术涉及塑料监工
，尤其涉及一种塑料喷涂技术。
技术介绍
随着塑料行业的迅猛发展，ABS塑料作为一种通用塑料，广泛应用于日用品、建筑、汽车制造业等领域。但由于ABS塑料在喷涂过程中对于其工艺过程及其参数处理不当，导致塑料涂层产生龟裂、起泡和脱落的问题，从而影响了塑料制品的使用寿命。
技术实现思路
为了解决塑料涂层产生龟裂、起泡和脱落的问题，本专利技术提供了一种ABS塑料喷涂工艺。本专利技术为实现上述目的所采用的技术方案是：一种ABS塑料喷涂工艺，包括以下步骤：（1）退火，把ABS塑料成型件加热到热变形60℃以下，保温1.5-2h；（2）除油，用清洗剂清洗，然后用纯水最后清洗干净，晾干或烘干；（3）除电及除尘，采用高压离子化空气流除电及除尘；（4）喷涂，塑料涂层厚度为15~20μm，喷涂2~3次，每次喷涂后晾干10-15min；（5）烘干，涂完后50-60℃条件下烘烤25-35min。所述步骤（2）中，清洗剂配方为：水为80%-90%，氢氧化钾为85％-95%，磷酸三钠为0.4%-0.6%，硅酸钠为2.5%-3.5%，磷酸盐化壬基苯氧...
【技术保护点】
一种ABS塑料喷涂工艺，其特征在于：包括以下步骤：（1）退火，把ABS塑料成型件加热到热变形60℃以下，保温1.5‑2h；（2）除油，用清洗剂清洗，然后用纯水最后清洗干净，晾干或烘干；（3）除电及除尘，采用高压离子化空气流除电及除尘；（4）喷涂，塑料涂层厚度为15~20μm，喷涂2~3次，每次喷涂后晾干10‑15min；（5）烘干，涂完后50‑60℃条件下烘烤25‑35min。
【技术特征摘要】
1.一种ABS塑料喷涂工艺，其特征在于：包括以下步骤：（1）退火，把ABS塑料成型件加热到热变形60℃以下，保温1.5-2h；（2）除油，用清洗剂清洗，然后用纯水最后清洗干净，晾干或烘干；（3）除电及除尘，采用高压离子化空气流除电及除尘；（4）喷涂，塑料涂层厚度为15~20μm，喷涂2~3次，每次喷涂后晾干10-15mi...
【专利技术属性】
技术研发人员：李忠有，
申请(专利权)人：大连裕丰塑料制品有限公司，
类型：发明
国别省市：辽宁,21