The invention discloses a heating coated sand and its preparation method, preparation method of coated sand heating of the present invention, which is characterized in that the powder preheating heating agent, silica sand 105 heated to 140 DEG C, they will be in the mixer mixing evenly, adding resin mixing 70 after 80S, and into the water solution mixing 30 Urotropine 50S, adding calcium stearate 70 100S after mixing sand molding. The heating medium strength of coated sand prepared by the invention, especially excellent gas, can make different shapes by heating the coated sand products, products shape easily after changes in shape, convenient assembly, good matching and casting products matching.
【技术实现步骤摘要】
一种发热覆膜砂及其制备方法
本专利技术涉及化工制造领域，具体涉及一种发热覆膜砂及其制备方法。
技术介绍
覆膜砂是指包覆着一层树脂膜砂粒的简称，它是一种铸造造型（芯）用材料，其形态在室温下多为干态分散的自然颗粒状。从广义上讲，覆膜砂也是一种树脂砂。现有发热覆膜砂，用作砂芯时发气量不够充分，无法改善铸件在浇注过程中冒口过早凝固封顶出现的铸件气孔和缩松缺陷。
技术实现思路
针对上述现有技术中存在的缺陷，本专利技术提供一种发热覆膜砂及其制备方法。本专利技术的发热覆膜砂发气量优异，可以发热，改善了铸件浇铸过程中局部发热作用，可制作成各种形状的砂芯，将其放置在充型后铁液局部需要延缓冷却的位置，解决了冒口过早凝固封顶出现的铸件气孔和缩松缺陷。具体地，本专利技术提供一种发热覆膜砂的制备方法，其将粉状发热剂预热，硅砂加热到105-140℃，将它们在混砂机混碾均匀后，加入树脂混碾70-80S后，加入乌洛托品水溶液混碾30-50S，再加入硬质酸钙混碾70-100S后放砂成型。此外，本专利技术的制备方法优选将粉状发热剂预热，硅砂加热到130℃，将它们在混砂机混碾均匀后，加入树脂混碾75S后，...
【技术保护点】
一种发热覆膜砂的制备方法，其特征在于，将粉状发热剂预热，硅砂加热到105‑140℃，将它们在混砂机混碾均匀后，加入树脂混碾70‑80S后，加入乌洛托品水溶液混碾30‑50S，再加入硬质酸钙混碾70‑100S后放砂成型。
【技术特征摘要】
1.一种发热覆膜砂的制备方法，其特征在于，将粉状发热剂预热，硅砂加热到105-140℃，将它们在混砂机混碾均匀后，加入树脂混碾70-80S后，加入乌洛托品水溶液混碾30-50S，再加入硬质酸钙混碾70-100S后放砂成型。2.根据权利要求1所述的制备方法，其特征在于，将粉状发热剂预热，硅砂加热到130℃，将它们在混砂机混碾均匀后，加入树脂混碾75S后，加入乌洛托品水溶液混碾40S，再加入硬质酸钙混碾90S后放砂成型。3.根据权利要求2所述的制备方法，其特征在于，所述硅砂与所述发热剂的重量比为。4.根据权利要求3所述的制备方法，其特征在于，所述硅砂与所述发热剂的重量比为53:47。...
【专利技术属性】
技术研发人员：田中青，田龙，张付，李冉，张启奎，张淑萍，
申请(专利权)人：西峡县众德汽车部件有限公司，
类型：发明
国别省市：河南,41