The invention discloses a method for preparing a ceramic film of silicon carbide powder with high sphericity, which comprises the following steps: (1) the pretreatment of silica fume; (2) silica precursor preparation; (3) carbide precursor; (4) silicon carbide calcination; step (3) system the type of carbon coated silica particles at high temperature and vacuum conditions, in accordance with the speed of 10 DEG /min is heated to 800 DEG C, 5 C according to the speed of /min is heated to 1300 to 1500 DEG C for calcination, holding 2 ~ 3H, natural cooling to room temperature, get silicon carbide powder. The invention has the characteristics of narrow size distribution, controllable and high ball shape.
【技术实现步骤摘要】
一种陶瓷膜用高球形度碳化硅粉体的制备方法
本专利技术属于无机非金属材料工程领域，具体涉及一种陶瓷膜用高球形度碳化硅粉体的制备方法。
技术介绍
碳化硅由于化学性能稳定、导热系数高、热膨胀系数小、耐磨性能好，除作磨料用外，在功能陶瓷、高级耐火材料及冶金原料等方面也有广阔的用途。特别是采用碳化硅制备无机陶瓷膜材料，凭借其耐高温，耐酸碱，化学稳定性好等诸多优点，广泛应用于纺织、电子、冶金、石油、工业废水、食品等多个领域。碳化硅作原料制备无机陶瓷膜材料，主要起到分离的作用，因此其分离效率的优劣是碳化硅陶瓷膜材料的关键指标，通常希望具有合适的孔径，较高的连通空隙率。因此，在理论上，为了保证合适的孔径和较高的连通空隙率，往往希望用于制备无机陶瓷膜的碳化硅粉体具有粒度分布窄，高球形度的特点。碳化硅天然含量甚少，碳化硅主要多为人造。常见的方法是将石英砂与焦炭混合，利用其中的二氧化硅和石油焦，加入食盐和木屑，置入电炉中，加热到2000℃左右高温，经过各种化学工艺流程后得到碳化硅微粉。在市场上，碳化硅通常用作磨料，因此其颗粒呈多边形，多棱角的特点，用于制备陶瓷膜材料，孔径和连通空隙率均...
【技术保护点】
一种陶瓷膜用高球形度碳化硅粉体的制备方法，其特征在于：它包括如下步骤：(1)硅粉的预处理a将硅粉，纤维素醚，水按照质量比200：1～8：1000混合，搅拌均匀后倒入量筒中，静置3min，取量筒二分之一液面以下的溶液，放入105℃的烘箱中得到烘干的硅粉；b将上述步骤得到的烘干硅粉与氢氟酸按照质量比1:1～10混合，静置24h后用蒸馏水清洗干净并烘干；(2)硅粉前驱体的制备将步骤(1)得到的硅粉与葡萄糖和蒸馏水按照质量比1:3.5～6:4～6.5混合搅拌30～45min，再置于90℃的水浴箱中20～30min，最后放入105℃的烘箱中干燥12～24h，将干燥后的样品研磨成粉获得...
【技术特征摘要】
1.一种陶瓷膜用高球形度碳化硅粉体的制备方法，其特征在于：它包括如下步骤：(1)硅粉的预处理a将硅粉，纤维素醚，水按照质量比200：1～8：1000混合，搅拌均匀后倒入量筒中，静置3min，取量筒二分之一液面以下的溶液，放入105℃的烘箱中得到烘干的硅粉；b将上述步骤得到的烘干硅粉与氢氟酸按照质量比1:1～10混合，静置24h后用蒸馏水清洗干净并烘干；(2)硅粉前驱体的制备将步骤(1)得到的硅粉与葡萄糖和蒸馏水按照质量比1:3.5～6:4～6.5混合搅拌30～45min，再置于90℃的水浴箱中20～30min，最后放入105℃的烘箱中干燥12～24h，将干燥后的样品研磨成粉获得硅粉前驱体；(3)前驱体的碳化将硅粉前驱体放入高...
【专利技术属性】
技术研发人员：徐慢，季家友，陈常连，
申请(专利权)人：湖北迪洁膜科技有限责任公司，
类型：发明