高耐磨性模具钢制造技术

本发明专利技术属于合金钢材料制备技术领域，尤其是涉及一种耐磨性能高的模具合金钢，具体公开了一种高耐磨性模具钢，该模具钢的成分及重量百分比为：C0.9~1.0%，Si0.6~1.1%，Mn0.2~0.5%，P≤0.025%，S≤0.02%，Cr7.7~8.2%，Mo0.7~1.0%，W0.3~0.6%，V0.05~0.15%，Ni0.35~0.55%，Cu0.2~0.4%，Nb0.05~0.15%，Al0.2~0.4%，余量为铁。采用本发明专利技术技术方案的模具钢，其耐磨性能高，价格低廉，热处理变形性小且可切削性强。

High wear resistant die steel

The invention belongs to the technical field of the preparation of alloy steel material, especially relates to a die alloy steel with high abrasion resistance, in particular discloses a mold of high wear-resistant steel, chemical composition and weight percentage of the die steel: C0.9~1.0%, Si0.6~1.1%, Mn0.2~0.5%, P = 0.025%, S = 0.02%, Cr7.7~8.2%, Mo0.7~1.0%, W0.3~0.6% V0.05~0.15%, Ni0.35~0.55%, Cu0.2~0.4%, Nb0.05~0.15%, Al0.2~0.4%, and the balance of iron. The die steel adopting the technical proposal of the invention has the advantages of high abrasion resistance, low price, small deformation of heat treatment and strong machinability.

【技术实现步骤摘要】

本专利技术属于合金钢材料制备
，尤其是涉及一种耐磨性能高的模具合金钢。
技术介绍
模具钢是用来制造冷冲模、热锻模压铸模等模具的钢种，模具是机械制造、无线电仪表、电机、电器等工业部门中制造零件的主要加工工具，模具的质量直接影响着压力加工工艺的质量、产品的精度产量和生产成本、而模具的质量与使用寿命除了靠合理的结构设计和加工精度外，主要受模具材料和热处理的影响。热作模具钢对硬度要求适当，侧重于红硬性，导热性，耐磨性。因此含碳量低，合金元素以增加淬透性，提高耐磨性、红硬性为主。热作模具工作条件的主要特点是与热态金属相接触、这是与冷作模具工作条件的主要区别，其模腔表面温度可达300～400℃以上，有点可达500~800℃以上，甚至达1000℃以上。这样高的使用温度会使模腔表面硬度和强度显著降低，在使用中易发生打垛。日本研发出的SKD11号工具钢，在业界最为知名，价格也最高，该钢广泛应用于冷作模具钢，经电炉冶炼并经电渣重溶，高纯净度，韧性更好，组织均匀，具有良好的高温强度、韧性与抗高温疲劳性能，能承受温度骤变，适宜在高温下长期工作，具有优良的切削性本文档来自技高网...

【技术保护点】
一种高耐磨性模具钢，其特征在于，该模具钢的成分及重量百分比为：C0.9~1.0%，Si0.6~1.1%，Mn0.2~0.5%，P≤0.025%，S≤0.02%，Cr7.7~8.2%，Mo0.7~1.0%，W0.3~0.6%，V0.05~0.15%，Ni0.35~0.55%，Cu0.2~0.4%，Nb0.05~0.15%，Al0.2~0.4%，余量为铁。

【技术特征摘要】
1.一种高耐磨性模具钢，其特征在于，该模具钢的成分及重量百分比为：C0.9~1.0%，Si0.6~1.1%，Mn0.2~0.5%，P≤0.025%，S≤0.02%，Cr7.7~8.2%，Mo0.7~1.0%，W0.3~0.6%，V0.05~0.15%，Ni0.35~0.55%，Cu0.2~0.4%，Nb0.05~0.15%，Al0.2~0.4%，余量为铁。
2.如权利要求1所述的高耐磨性模具钢，其特征在于，C0.9%，Si0.6%，Mn0.2%，P0.01%，S0.01%，Cr7.7%，Mo0.7%，W0.3%，V0....

【专利技术属性】
技术研发人员：朱小坤，张卫国，
申请(专利权)人：天工爱和特钢有限公司，
类型：发明
国别省市：江苏;32