The present invention provides a kind of waterborne anticorrosive coatings, by weight, consists of the following components: acrylic resin 20 25, B two 1 aldehyde 2, pentaerythritol 10 15 copies, 20 copies, 15 cyclohexanone OCTYL METHACRYLATE 10 15, 0.5 2 alkyd resin A, anti oxidant 0.2 0.5 copies, 2 copies, 1 lignin aqueous thickener 0.5 2, deionized water allowance. Anticorrosive coating prepared by the invention can be directly against the construction of water, avoid or reduce the use of carbon containing organic solvent, both the environmental protection and resource conservation, taking water as the medium, safe, non-toxic, will not cause harm to human body.
【技术实现步骤摘要】
一种水性防腐涂料及其制备方法
本专利技术涉及涂料领域,具体涉及一种水性防腐涂料及其制备方法。
技术介绍
随着涂料工业和涂装工艺向低污染化发展,水性涂料正在日益兴起。水性涂料减少了有机溶剂对环境造成的危害与污染,保障了操作人员的身体健康,降低了涂料的生产成本,便于工厂采取安全措施和运输,同时又便于工具的清洗。安全、环保、无公害、挥发性有机物(VOC)排放少的绿色环保涂料,非常具有研制开发的必要,亦具有广泛的应用前景。凡是用水作溶剂或者作分散介质的涂料,都可称为水性涂料。水性涂料以水作为分散介质,仅采用少量低毒性醇醚类有机溶剂,安全环保、节约资源,消除了施工时发生火灾的危险性,有利于降低大气污染。水性涂料对材质表面适应性非常好,在潮湿环境同样可以施工,涂层附着力强。
技术实现思路
为解决上述技术问题,本专利技术的目的是提供一种优异的防护装饰效果、防锈性和耐水性、性能稳定、附着力强的水性防腐涂料及其制备方法。为实现本专利技术的目的,本专利技术采用如下技术方案:一种水性防腐涂料,以重量份数计,由以下组份组成:丙烯酸树脂20-25份、乙二醛1-2份、季戊四醇10-15份、环己酮15-20份、甲基丙烯酸异辛酯10-15份、醇酸树脂0.5-2份、抗氧化剂0.2-0.5份、木质素1-2份、水性增稠剂0.5-2份、去离子水余量。作为优选,所述的一种水性防腐涂料,其特征在于,所述的水性增稠剂为聚氨酯类增稠剂。作为优选,所述的一种水性金属防腐材料,其特征在于,所述的环己酮固体含量为88±2%。作为优选,所述的一种水性防腐涂料,其特征在于包括如下步骤:(1)在干燥氮气气体的保护下,将 ...
【技术保护点】
一种水性防腐涂料,以重量份数计,由以下组份组成:丙烯酸树脂20‑25份、乙二醛1‑2份、季戊四醇10‑15份、环己酮15‑20份、甲基丙烯酸异辛酯10‑15份、醇酸树脂0.5‑2份、抗氧化剂0.2‑0.5份、木质素1‑2份、水性增稠剂0.5‑2份、去离子水余量。
【技术特征摘要】
1.一种水性防腐涂料,以重量份数计,由以下组份组成:丙烯酸树脂20-25份、乙二醛1-2份、季戊四醇10-15份、环己酮15-20份、甲基丙烯酸异辛酯10-15份、醇酸树脂0.5-2份、抗氧化剂0.2-0.5份、木质素1-2份、水性增稠剂0.5-2份、去离子水余量。2.根据权利要求1所述的一种水性防腐涂料,其特征在于,所述的水性增稠剂为聚氨酯类增稠剂。3.根据权利要求1所述的一种水性金属防腐材料,其特征在于,所述的环己酮固体含量为88±2%。4.根据权利要求1所述的一种水性防腐涂料,其特征在于包括如下步...