The invention discloses a lubricant, including: Vulcanized cottonseed oil 7, petroleum sulfonate 3, fourteen alkyl three methyl ammonium chloride 5, stannous sulfate 3, two isopropyl naphthalene sulfonic acid sodium carboxymethyl cellulose, 3 3, two two 6 diethylene glycol butyl ether, butyl titanate, antiwear agent, water 15 5 1000; the invention of antiwear agent added to improve the heat dissipation effect of nano aluminum nitride powder at the end, to enhance the cooling effect, increase the film, prolong the service life of dies; the invention has good lubricating property and lubricant low production cost, product drawing light, the products are widely used in lubricant products, galvanized nickel plated copper and chromium plated products and other products.
【技术实现步骤摘要】
一种拉丝润滑剂
本专利技术涉及润滑剂领域，特别是一种拉丝润滑剂。
技术介绍
拉丝工艺是一种金属加工工艺。在金属压力加工中，在外力作用下使金属强行通过模具，金属横截面积被压缩，并获得所要求的横截面积形状和尺寸的技术加工方法称为金属拉丝工艺。使其改变形状、尺寸的工具称为拉丝模。目前，市场上的拉丝用润滑剂存在着产品品种少，使用效果不太理想以及生产成本高的问题，这种状况影响了拉丝产品的发展。
技术实现思路
为了实现本专利技术的目的，本专利技术提供一种生产成本低、使用效果好的拉丝润滑剂及其制作方法。本专利技术的润滑剂包括硫化棉籽油7、石油磺酸钠3、十四烷基三甲基氯化铵5、硫酸亚锡3、二异丙基萘磺酸钠3、羧甲基纤维素3、二甘醇二丁醚6、钛酸丁酯5、抗磨剂15、水1000；所述抗磨剂由下列重量份的原料制成：硅藻土2.8、玉石2、乌洛托品2.5、尿素0.9、硅烷偶联剂KH-5501.5、十二烷基苯磺酸钠0.3、抗坏血酸3、硫磺粉3、纳米氮化铝粉末1.8、水75；制备方法是将玉石、硅藻土送入580℃煅烧炉中，煅烧5小时，冷却后粉碎放入18%盐酸溶液中浸泡5小时，取出，洗涤干净，烘干研磨...
【技术保护点】
一种拉丝润滑剂，其特征在于，由下列重量份的原料制成：硫化棉籽油7、石油磺酸钠3、十四烷基三甲基氯化铵5、硫酸亚锡3、二异丙基萘磺酸钠3、羧甲基纤维素3、二甘醇二丁醚6、钛酸丁酯5、抗磨剂15、水1000；所述抗磨剂由下列重量份的原料制成：硅藻土2.8、玉石2、乌洛托品2.5、尿素0.9、硅烷偶联剂KH‑550 1.5、十二烷基苯磺酸钠0.3、抗坏血酸3、硫磺粉3、纳米氮化铝粉末1.8、水75；制备方法是将玉石、硅藻土送入580℃煅烧炉中，煅烧5小时，冷却后粉碎放入18%盐酸溶液中浸泡5小时，取出，洗涤干净，烘干研磨550目粉末，与其它剩余成分混合，加热至80℃，在1800转...
【技术特征摘要】
1.一种拉丝润滑剂，其特征在于，由下列重量份的原料制成：硫化棉籽油7、石油磺酸钠3、十四烷基三甲基氯化铵5、硫酸亚锡3、二异丙基萘磺酸钠3、羧甲基纤维素3、二甘醇二丁醚6、钛酸丁酯5、抗磨剂15、水1000；所述抗磨剂由下列重量份的原料制成：硅藻土2.8、玉石2、乌洛托品2.5、尿素0.9、硅烷偶联剂KH-5501.5、十二烷基苯磺酸钠0.3、抗坏血酸3、硫磺粉3、纳米氮化铝粉末1.8、水75；制备方...
【专利技术属性】