The invention discloses a coupling graft graphene reinforced modified conductive nylon 6, which is characterized in that the water bath to the carbon fiber with acetone, concentrated nitric acid, and water to neutral; to KH550 in ethanol, mixing, adding carbon fiber after washing, mixing, drying to hydroxyl group; carbon nanotubes, polyvinylpyrrolidone and deionized water to hydroxylation of carbon nanotubes in aqueous solution; water solution by the method of vacuum impregnation into the carbon fiber, freeze drying, heat treatment; to graphene with mixed acid, reaction, oil bath diluted with water, filtering, washing, vacuum drying; to ethanol plus KH570, mixed liquid; adding the acid graphene, a constant temperature water bath reaction, acetone cleaning and filtration; the dried nylon 6, plasticizer and C in the material blending, the resulting blend from the main The hopper is added to the twin screw extruder, and the material added to the B is added to the material to be extruded and blended, and then the granulator is cut into pellets by cooling.
【技术实现步骤摘要】
一种偶联接枝石墨烯增强改性的导电型尼龙6及其制备方法
本专利技术涉及复合材料领域，具体涉及一种偶联接枝石墨烯增强改性的导电型尼龙6的制备方法。
技术介绍
热塑性树脂复合材料具有可重复回收利用、加工成型快等优点，近些年来在复合材料领域中一直受到广泛关注。尼龙是由己内酰胺开环聚合而成的一种聚合物，是目前应用最广泛的的合成纤维之一。但传统的尼龙纤维已经不能再满足人们的需求，在这种情况下，如何开发高性能的尼龙纤维，引起人们越来越多的关注。
技术实现思路
本专利技术主要解决的技术问题是提供一种偶联接枝石墨烯增强改性的导电型尼龙6的制备方法，依照该工艺制备的复合材料具有良好的导电性能、力学性能和弯曲强度。本专利技术所要解决的技术问题采用以下的技术方案来实现：一种偶联接枝石墨烯增强改性的导电型尼龙6的制备方法，其特征在于，按以下步骤进行：a.碳纤维清洗脱胶、液相氧化与硅烷偶联剂复合改性工艺：向7-8重量份碳纤维中1:5-10加入丙酮，超声处理1-2h后，1:5-10加入浓硝酸，在60-70℃恒温水浴5-6h，用蒸馏水清洗至pH为中性；向0.1-0.2重量份硅烷偶联剂KH550中1:...
【技术保护点】
一种偶联接枝石墨烯增强改性的导电型尼龙6，其特征在于：向碳纤维中加丙酮、浓硝酸，水浴，水洗至中性；向KH550中加乙醇，混合均匀，加入水洗后的碳纤维，混匀，干燥；向羟基化碳纳米管、聚乙烯吡咯烷酮中加去离子水，得羟基化碳纳米管水溶液；将水溶液通过真空浸渍的方法引入到所得碳纤维中，冷冻干燥，热处理；向石墨烯中加混酸，油浴中反应，加水稀释，抽滤，水洗，真空干燥；向无水乙醇中加KH570，配成混合液；加入上述酸化石墨烯，恒温水浴反应，丙酮清洗，抽滤；将干燥的尼龙6、增塑剂与c中所得物料混合均匀，将所得共混物从主料斗加入双螺杆挤出机中，从料口加入b中所得物料，挤出共混，冷却后由造粒机切成粒料。
【技术特征摘要】
1.一种偶联接枝石墨烯增强改性的导电型尼龙6，其特征在于：向碳纤维中加丙酮、浓硝酸，水浴，水洗至中性；向KH550中加乙醇，混合均匀，加入水洗后的碳纤维，混匀，干燥；向羟基化碳纳米管、聚乙烯吡咯烷酮中加去离子水，得羟基化碳纳米管水溶液；将水溶液通过真空浸渍的方法引入到所得碳纤维中，冷冻干燥，热处理；向石墨烯中加混酸，油浴中反应，加水稀释，抽滤，水洗，真空干燥；向无水乙醇中加KH570，配成混合液；加入上述酸化石墨烯，恒温水浴反应，丙酮清洗，抽滤；将干燥的尼龙6、增塑剂与c中所得物料混合均匀，将所得共混物从主料斗加入双螺杆挤出机中，从料口加入b中所得物料，挤出共混，冷却后由造粒机切成粒料。2.一种偶联接枝石墨烯增强改性的导电型尼龙6的制备方法，其特征在于：a.碳纤维清洗脱胶、液相氧化与硅烷偶联剂复合改性工艺：向7-8重量份碳纤维中1:5-10加入丙酮，超声处理1-2h后，1:5-10加入浓硝酸，在60-70℃恒温水浴5-6h，用蒸馏水清洗至pH为中性；向0.1-0.2重量份硅烷偶联剂KH550中1:10-20加入乙醇，混合均匀，加入上述水洗后的碳纤维，超声振荡搅拌、充分混匀，静置过夜，放入100-115℃烘箱中干燥3-4h；b.碳纳米管改性碳纤维及冷冻干燥工艺：向2-3重量份羟基化碳纳米管、1-3重量份聚乙烯吡咯烷酮中加入去离子水，磁力搅拌1-2h、超声振荡1-2h混合均匀，得质量分数为0.5-1%的羟基化碳纳米管水溶液；将上述水溶液通过真空浸渍的方法引入到a中所得碳纤维中，在零下15-20℃冷柜中冷冻5-6h后，在冷冻干燥机上冷冻干燥至真空度低于17-20Pa，然...
【专利技术属性】
技术研发人员：宋睿，王贵东，
申请(专利权)人：合肥新意境材料有限责任公司，
类型：发明
国别省市：安徽,34