一种新型电缆保护皮及其制作工艺制造技术

本发明专利技术提供一种新型电缆保护外皮及其制作工艺，其成分包括：丙烯酸树脂、硅橡胶、聚乙烯蜡、硅酸钾、碳酸钙、阻燃剂、稳定剂和增塑剂，将上述成分混合搅拌在一起，将材料加热一段时间再降温，溶解后涂敷在电缆上塑型形成保护套。本发明专利技术具有良好的机械强度，还具有生产成本低，生产效率高的特点，对环境无毒、无污染。

Novel cable protection leather and manufacturing process thereof

The present invention provides a new type of cable sheath and its manufacturing process and its components include: acrylic resin, silicone rubber, polyethylene wax, potassium silicate, calcium carbonate, flame retardant, stabilizer and plasticizer, the components are mixed together, the material is heated for a period of time and then cooling, after dissolving the coating on the cable the formation of plastic protective sleeve. The invention has good mechanical strength, and has the characteristics of low production cost and high production efficiency, and is non-toxic and pollution-free to the environment.

【技术实现步骤摘要】
一种新型电缆保护皮及其制作工艺
本专利技术属于电线电缆保护套的制备
，具体涉及一种新型电缆保护外皮及其制作工艺。
技术介绍
随着社会化的不断进步，电力业已成为国民经济快速发展的重要支柱。电线电缆的使用在逐年增加，随之而来的电线电缆的损坏问题也在日益增多。因此，对电线电缆的保护提出的要求也越来越高，电线电缆保护套是最常用的一种电绝缘保护方式，其绝缘性好、化学稳定性高、不生锈、可适应苛刻环境而被广泛的应用，但是保护套还需要优良的物理性能，如拉伸强度、断裂伸长率等性能。随着我国经济的发展，通信技术、广播电视、铁路交通、石油化工、建筑等领域也有了较大的进步。各种电线电缆，通信电缆等在这些领域中被普遍使用，并且成为必不可少的组成部分之一。然而在高寒地区或者寒冷环境条件下的设施，对此类产品的阻燃、耐低温的性能和使用寿命、质量、适用性提出了更高的要求。但是现在的保护套仍然满足不了一些特殊情况的保护，因此需要一种更好的保护套，来改善现有技术的不足。
技术实现思路
本专利技术的目的是提供一种新型电缆保护外皮及其制作工艺，本专利技术具有生产成本低，生产效率高的特点，对环境无污染。本专利技术提供了如下的本文档来自技高网...

【技术保护点】
一种新型电缆保护外皮，其特征在于，包括以下重量份的原料：丙烯酸树脂20‑30份、硅橡胶15‑28份、聚乙烯蜡10‑24份、硅酸钾12‑23份、碳酸钙5‑13份、阻燃剂3‑8份、稳定剂15‑22份和增塑剂16‑29份。

【技术特征摘要】
1.一种新型电缆保护外皮，其特征在于，包括以下重量份的原料：丙烯酸树脂20-30份、硅橡胶15-28份、聚乙烯蜡10-24份、硅酸钾12-23份、碳酸钙5-13份、阻燃剂3-8份、稳定剂15-22份和增塑剂16-29份。2.根据权利要求1所述的一种新型电缆保护外皮，其特征在于，包括以下重量份的原料：丙烯酸树脂30份、硅橡胶19份、聚乙烯蜡22份、硅酸钾16份、碳酸钙11份、阻燃剂3份、稳定剂22份和增塑剂16份。3.根据权利要求1所述的一种新型电缆保护外皮，其特征在于，所述阻燃剂为氢氧化镁与硼酸锌的混合物。4.根据权利要求1所述的一种新型电缆保护外皮，其特征在于，所述增塑剂为磷酸二苯异辛酯和磷酸二苯异丙苯酯的混合物。5.权利要求1-4任一项所述的一种新型电缆保护外皮的制作工艺，其特征在于，步骤如下：步骤一、将硅橡胶、聚乙烯蜡、硅酸钾和碳酸钙捣...