本实用新型专利技术提供一种可钎焊和耐腐蚀的马口铁，属于马口铁结构领域。本实用新型专利技术包括基板、分别覆盖在所述基板上下表面上的镀锡层、覆盖在所述镀锡层上的钝化膜层和设置在所述钝化膜层上的油膜层。本实用新型专利技术的有益效果为：材料表面因游离锡层厚度较高，具有良好的钎焊性能，本实用新型专利技术材料具备高钎焊、强抗腐蚀性能，可代替Ni基材料应用于电子零件用途，节省稀有、贵重金属，降低了成本。

A brazed and corrosion-resistant tinplate

The utility model provides a soldering tin capable of soldering and corrosion resistance, which belongs to the tinplate structure field. The utility model comprises a base plate, a tin coating covered on the upper and the lower surfaces of the substrate, a passivation film covered on the tin plating layer and an oil film layer disposed on the passivation film layer. The utility model has the advantages that: the material surface due to the free tin layer thickness is high, with good brazing performance, the utility model has the advantages of material with high brazing, strong corrosion resistance, can replace the Ni based materials used in electronic parts usage, rare and precious metal saving, reduced cost.

【技术实现步骤摘要】
一种可钎焊和耐腐蚀的马口铁
本技术涉及一种马口铁结构，尤其涉及一种可钎焊和耐腐蚀的马口铁。
技术介绍
电子零件用途的材料需要良好的钎焊以及抗腐蚀性能，一般多采用Ni基材料，但是，金属Ni为稀有、贵重金属，价格昂贵，难以推广、普及。而一般马口铁材料难以满足高钎焊性能以及高抗腐蚀性能的要求。一般经软熔的马口铁材料，因表面镀锡层厚度不足，所以钎焊性能不佳。同时在软熔合金层环节，基板的铁元素会向镀锡层迁移，导致镀锡层露铁程度加重(ISV水平提高)，所以盐雾试验的表现也较差。一般经软熔的材料在钎焊性以及耐蚀性方面难以满足电子零件材料的要求。
技术实现思路
为解决现有技术中的问题，本技术提供一种可钎焊和耐腐蚀的马口铁。本技术包括基板、分别覆盖在所述基板上下表面上的镀锡层、覆盖在所述镀锡层上的钝化膜层和设置在所述钝化膜层上的油膜层。本技术作进一步改进，所述镀锡层的厚度为2.8～19.0克/平方米。本技术作进一步改进，所述镀锡层的厚度为5～16.0克/平方米。本技术作进一步改进，所述镀锡层的厚度为11.2克/平方米。本技术作进一步改进，所述钝化膜层的原料为重铬酸钠和铬酸。本技术作进一步改进，所述钝化膜层中铬本文档来自技高网...

【技术保护点】
一种可钎焊和耐腐蚀的马口铁，其特征在于：包括基板、分别覆盖在所述基板上下表面上的镀锡层、覆盖在所述镀锡层上的钝化膜层和设置在所述钝化膜层上的油膜层。