X型坡口立缝焊接的方法技术
X groove vertical seam welding method
The invention discloses a X type groove vertical welding method of the invention of the X type welding groove of backing welding way, using GMAW, in one side welding groove on both sides of the first welding, the other side of the pool is not completely cooled under the condition of constant welding, until backing after the completion of welding, welding layer on both sides, until all welding seam. Vertical welding method saves root cleaning and cleaning the root after the grinding process of the present invention, to significantly enhance the efficiency and avoid the welding defects caused by root cleaning is not complete and other factors, the welding quality significantly, weld angular distortion has been effectively controlled.
【技术实现步骤摘要】
X型坡口立缝焊接的方法
本专利技术涉及一种X型坡口立缝焊接的方法。
技术介绍
传统X型坡口立焊方法如图1、图2所示，先焊接一侧直至坡口深度的1/3或够清根量，在另一侧用碳弧气刨进行清根、清根后需用砂轮机或旋转锉等工具打磨再进行焊接，因清根、清磨带来的变形大，辅助工作时间长，焊接质量难以保证。因焊接时为手工操作，对焊工技能要求相对较高，易产生焊接缺陷。
技术实现思路
本专利技术提供一种焊接质量好、工作效率高的X型坡口立缝焊接的方法。本专利技术的技术方案为：一种X型坡口立缝焊接的方法，1)对第一母材(1)与第二母材(2)之间的立焊坡口(3)进行打底焊接，打底焊接的方式为，采用熔化极气体保护焊，在立焊坡口(3)两侧的一侧先进行焊接，另一侧熔池未完全冷却的状态下进行等速焊接，直至打底焊接完成；2)在立焊坡口(3)两侧逐层焊接，直至焊缝全部焊接完成。技术效果：本专利技术采用焊工对称等速先后焊接，代替传统的先焊接一侧、再进行清根打磨的焊接方法。具有以下优点:1)传统的X型坡口立缝焊接的方法，先焊接第一侧直至坡口深度的1/3或够清根量，在第二侧用碳弧气刨进行清根、清根后需用砂轮机或旋转锉等工具打磨再进行焊接，因清根、清磨带来的变形大，辅助工作时间长，焊接质量难以保证。传统X型坡口立缝焊接方法清根、清磨两道工序的目的第一是清除第一侧焊缝根部的缺陷,如气孔、凹坑、杂质等，其二是在第二侧制备出合适的焊接坡口(原坡口已经被第一侧焊缝破坏)。本专利提出的方法，在立焊坡口(3)两侧的一侧先进行焊接，另一侧熔池未完全冷却的状态下进行等速焊接，直至打底焊接完成，由于熔池未完全冷却就在背面另...
【技术保护点】
一种X型坡口立缝焊接的方法，其特征是：1)对第一母材(1)与第二母材(2)之间的立焊坡口(3)进行打底焊接，打底焊接的方式为：采用熔化极气体保护焊，在立焊坡口(3)两侧的一侧先进行焊接，另一侧熔池未完全冷却的状态下进行等速焊接，直至打底焊接完成；2)在立焊坡口(3)两侧逐层焊接，直至焊缝全部焊接完成。
【技术特征摘要】
1.一种X型坡口立缝焊接的方法，其特征是：1)对第一母材(1)与第二母材(2)之间的立焊坡口(3)进行打底焊接，打底焊接的方式为：采用熔化极气体保护焊，...
【专利技术属性】
技术研发人员：林磊，魏方锴，夏振国，徐睦忠，张伟华，乔宏来，闫海滨，甘洪丰，段伟赞，叶鸿森，曹瀚，
申请(专利权)人：哈尔滨电机厂有限责任公司，
类型：发明
国别省市：黑龙江,23