A kind of arsenic poisoning SCR denitration catalyst regeneration method, its main contents include: firstly, arsenic poisoning SCR denitration catalyst ground into powder; then the catalyst powder impregnated with regeneration liquid, 2 hours of reaction time, meet the regeneration liquid acetic acid and sodium carbonate concentration are 1mol/L; separated from the regenerated catalyst and repeatedly cause the cleaning solution pH to 6.5 7 rinse with deionized water; the regenerated catalyst is placed in the constant temperature drying box, 110 drying for 12 hours, the regeneration of SCR denitration catalyst is obtained. The invention is characterized in that the raw material of the reclaimed liquid is easy to obtain, the economic cost is low, the energy consumption is small, the preparation process is simple, and no two pollution can be caused.
【技术实现步骤摘要】
一种砷中毒SCR脱硝催化剂的再生方法所属
本专利技术属于SCR脱硝催化剂再生领域，具体涉及一种砷中毒SCR脱硝催化剂的再生方法。
技术介绍
目前，我国燃煤电厂占全国发电量70％以上，选择性催化还原法(SCR)烟气脱硝技术作为最成熟烟气脱硝技术之一，广泛应用于国内外燃煤电厂。SCR催化剂作为SCR脱硝技术的核心，设计寿命约为24000小时，会随着运行时间的增加活性逐渐降低。引起催化剂活性降低的原因有催化剂中毒、催化剂烧结和活性组分流失等问题，最终导致催化剂失活。然而，引起催化剂中毒的物质主要有碱金属、碱土金属、磷、重金属、HCl等。由于我国多数煤种含砷量比较高，燃煤电厂煤燃烧会释放出煤中的大部分砷并存在于烟气中。烟气中的砷会在SCR脱硝系统中脱除氮氧化物的同时致使催化剂重金属砷中毒，从而降低SCR催化剂的活性，影响脱硝效率。燃煤电厂每年更换废弃催化剂，不仅增加脱硝运行系统成本，还给环境带来沉重的负担。废弃催化剂量逐年递增，再生废弃SCR催化剂，显得尤为重要。研究重金属砷中毒的SCR催化剂，并对其进行再生，将对废弃催化剂的回收利用有着很大的实际价值，利于实现有限资源的...
【技术保护点】
一种砷中毒SCR脱硝催化剂的再生方法，其特征在于，该方法包括以下几个步骤：(1)、将砷中毒SCR脱硝催化剂研磨过筛；(2)、将步骤(1)所得砷中毒催化剂粉末放入再生液中浸渍再生；(3)、将步骤(2)所得再生催化剂与再生液分离，再用去离子水多次冲洗；(4)、将步骤(3)所得再生催化剂，放入恒温鼓风干燥箱烘干，即得到再生的SCR脱硝催化剂。
【技术特征摘要】
1.一种砷中毒SCR脱硝催化剂的再生方法，其特征在于，该方法包括以下几个步骤：(1)、将砷中毒SCR脱硝催化剂研磨过筛；(2)、将步骤(1)所得砷中毒催化剂粉末放入再生液中浸渍再生；(3)、将步骤(2)所得再生催化剂与再生液分离，再用去离子水多次冲洗；(4)、将步骤(3)所得再生催化剂，放入恒温鼓风干燥箱烘干，即得到再生的SCR脱硝催化剂。2.根据权利要求1所述的一种砷中毒SCR脱硝催化剂的再生方法，其特征在于：所述的步骤(1)中，将砷中毒SCR脱硝催化剂研磨过筛，粒径满足20-40目。3.根...
【专利技术属性】
技术研发人员：齐立强，陈凤桥，徐珺，姚远，
申请(专利权)人：华北电力大学保定，
类型：发明
国别省市：河北,13