The invention provides a waterproof porous foamed PVC plate suitable for pervious concrete in order to prevent the pore blockage of pervious concrete, so as to prolong the service life and range of pervious concrete. The permeable porous foamed PVC board, composed of the following raw materials in weight portion: 10 55 PVC, 14 30 emulsified asphalt, 5 15 calcium oxide, 10 20 10 20 copies of loose powder, soap, 1 5 pigment. The permeable porous foamed PVC board thickness of 1 4cm diameter is 1; 4mm; volume porosity of 15 25%; permeability coefficient is 1 6mm/s. The prepared as anti blocking sheet layer is smaller than the pore size of concrete pore size, can effectively filter the dust, to prevent clogging of pervious concrete; foaming speed, high porosity, high permeability, can rapid permeability; do choose latex adhesive, once thin pore plugging, simple replacement sheet.
【技术实现步骤摘要】
一种透水多孔发泡PVC板及其生产方法和应用
本专利技术涉及了一种透水多孔发泡PVC板及其生产方法和应用，属于材料科学领域。
技术介绍
随着社会经济的发展和城市建设的进程，现代城市的地表逐步被钢筋混凝土的房屋建筑和不透水的路面所覆盖，现代化地表给城市带来一系列的问题，如不透水的路面阻碍了雨水的下渗，使得雨水对地下水的补充被阻断，再加上地下水的过度抽取，城市地面容易产生下沉；不透水路面使城市空气湿度降低，加速了城市热岛效应的形成。透水混凝土又称多孔混凝土或无砂混凝土，由粗骨料表面包覆一薄层水泥浆相互粘结而形成孔穴均匀分布的蜂窝状结构，故具有透气、透水和重量轻的特点。是保护地下水、维护生态平衡、能缓解城市热岛效应的优良的铺装材料；其有利于人类生存环境的良性发展及城市雨水管理与水污染防治等工作上，具有特殊的重要意义。但是，在透水混凝土服役期间，孔隙堵塞问题被发现，并严重影响着其广泛使用，目前尚无有效解决办法。
技术实现思路
本专利技术的目的是针对透水混凝土孔隙堵塞问题，提供一种适用于透水混凝土的防塞的透水多孔发泡PVC板，以延长透水混凝土的使用期限及范围。本专利技术另一目的是...
【技术保护点】
一种透水多孔发泡PVC板，其特征在于，由以下重量份的原料组成：10‑55份聚氯乙烯，14‑30份乳化沥青，5‑15份氧化钙，10‑20份铝粉，10‑20份松香皂，1‑5份颜料；所述多孔薄板的厚度为1‑4cm；孔径为1‑4mm；体积孔隙率为15‑25%，透水系数为1‑6mm/s。
【技术特征摘要】
1.一种透水多孔发泡PVC板，其特征在于，由以下重量份的原料组成：10-55份聚氯乙烯，14-30份乳化沥青，5-15份氧化钙，10-20份铝粉，10-20份松香皂，1-5份颜料；所述多孔薄板的厚度为1-4cm；孔径为1-4mm；体积孔隙率为15-25%，透水系数为1-6mm/s。2.一种如权利要求1或2所述的透水多孔发泡PVC板的生产方法，其特征在于，采用以下步骤生产：（1）按比例将将除乳胶外的原料混合均匀，在保温箱发泡，并切割成薄板，用气流穿过薄板；（2）在薄板四周边缘喷涂乳胶得到透水多孔发泡PVC板。3.根据权利要求3所述的生产方法，其特征在于，气流的温度为40-60℃，压...
【专利技术属性】
技术研发人员：宫晨琛，代文燕，芦令超，程新，
申请(专利权)人：济南大学，
类型：发明
国别省市：山东,37