The invention discloses a roller compacted concrete and its preparation method, the RCC consists of the following parts by weight of raw materials prepared by cement: 100; fly ash: 90 ~ 110; metakaolin: 40 ~ 70; water: 110 ~ 140; river sand: 850 ~ 900; stone: from 1950 to 2050; 1 to 3 parts: water reducer. The preparation method of the roller compacted concrete is as follows: cement, fly ash, metakaolin, water, river sand, crushed stone and water reducing agent are added into the mixer successively, stirring 3 ~ 5min, and then the roller compacted concrete is obtained. The invention replaces the traditional river sand mechanism sand preparation of roller compacted concrete, reduce the production cost, gradation and add metakaolin to improve river sand, increase the content of fine powder, RCC can grind, pan pulp, anti permeability and physical strength improved significantly.
【技术实现步骤摘要】
一种碾压混凝土及其制备方法
本专利技术涉及一种碾压混凝土及其制备方法，属于建筑材料
技术介绍
碾压混凝土是一种干硬性贫水泥的混凝土，常利用碾压机械进行碾压施工，由于其水泥用量小，有利于混凝土温控防裂和机械化作业，常用于水工大坝。碾压混凝土中的细骨料大多采用机制砂，主要是因为机制砂中的细粉含量可调，细骨料中含有较高比例的细粉是保证碾压混凝土可碾性和碾压泛浆性的基础，对碾压混凝土的质量有着重要影响。然而，机制砂的生产成本较高，在很大程度上限制了其广泛应用。天然河砂是主要的建筑原材料，常用于拌制混凝土和水泥砂浆，但由于其含粉量少，拌制碾压混凝土时，其可碾性、泛浆性很差，所以碾压混凝土拌制一般不采用天然河砂。因此，有必要开发一种性能优异、生产成本低的碾压混凝土。
技术实现思路
本专利技术的目的在于提供一种碾压混凝土及其制备方法。本专利技术所采取的技术方案是：一种碾压混凝土，其由以下质量份的原料制备而成：水泥：100份；粉煤灰：90～110份；偏高岭土：40～70份；水：110～140份；河砂：850～900份；碎石：1950～2050份；减水剂：1～3份。所述的水泥...
【技术保护点】
一种碾压混凝土，其特征在于：其由以下质量份的原料制备而成：水泥：100份；粉煤灰：90～110份；偏高岭土：40～70份；水：110～140份；河砂：850～900份；碎石：1950～2050份；减水剂：1～3份。
【技术特征摘要】
1.一种碾压混凝土，其特征在于：其由以下质量份的原料制备而成：水泥：100份；粉煤灰：90～110份；偏高岭土：40～70份；水：110～140份；河砂：850～900份；碎石：1950～2050份；减水剂：1～3份。2.根据权利要求1所述的碾压混凝土，其特征在于：所述的水泥为硅酸盐水泥。3.根据权利要求1所述的碾压混凝土，其特征在于：所述的粉煤灰的粒径小于45μm。4.根据权利要求1所述的碾压混凝土，其特征在于：所述的偏高岭土由高岭土在800℃～950℃的条件下煅烧2～2.5小时制成，平均粒径≤10μm，SiO2和Al2O3总的质量百分含量≥85%。5.根据权利要求1所述的碾压混凝土，其特征...