The invention discloses a free surface treatment and coating cracking air drum plastering mortar and construction method thereof, by weight, anti cracking mortar air drum comprises the following components: common portland cement: 100 ~ 160; sand: 680 ~ 890; fly ash: 0 ~ 200; polymer adhesive: 1 - 3; 5 to 10 parts: compound admixture; fiber: 0.9 ~ 15. The construction method comprises the following steps: in accordance with the ratio of weighting material mixing, on the basis of the construction of thick mortar mixed with proper amount of water and air defense anti cracking mortar drum evenly; the anti crack plastering mortar spraying machine with air drum directly sprayed on the surface of the building construction or directly plastering construction in the construction of buildings on the surface. After curing is made of plaster mortar.
【技术实现步骤摘要】
免基面处理且可喷涂的抗裂防空鼓抹灰砂浆及其施工方法
本专利技术涉及建筑材料的
，更具体地讲，涉及一种免基面处理且可喷涂的抗裂防空鼓抹灰砂浆及其施工方法。
技术介绍
抹灰砂浆涂抹在建筑物墙面、顶面、地面和柱表面能够起到找平、防水、防护和装饰作用建筑材料的作用。但是，传统的抹灰砂浆抗压强度高、粘结强度低且硬脆，并且由于其水泥用量大、砂浆拌合用水量大、砂浆拌合物失水快、抹灰层砂浆失水和水泥水化收缩大等问题，导致涂抹之后的抹灰砂浆层经常出现裂纹和与基层脱开产生空鼓等问题，因此在吸水率低或光滑表面的基材上进行抹灰施工之前必须预先进行机械拉毛或甩浆处理增加表面粗糙度后方可进行抹灰施工。此外，传统抹灰砂浆的保水性差，对于吸水性强的基材，则需要预先对基材进行浸水处理后才能进行抹灰施工。
技术实现思路
为了解决现有技术中存在的问题，本专利技术的目的是提供一种能够免基面处理且可喷涂的抗裂防空鼓抹灰砂浆及其施工方法。本专利技术的一方面提供了一种免基面处理且可喷涂的抗裂防空鼓抹灰砂浆，以重量份计，所述抗裂防空鼓抹灰砂浆包括以下组分：通用硅酸盐水泥：100～160份；砂：680～890份...
【技术保护点】
一种免基面处理且可喷涂的抗裂防空鼓抹灰砂浆，其特征在于，以重量份计，所述抗裂防空鼓抹灰砂浆包括以下组分：通用硅酸盐水泥：100～160份；砂：680～890份；粉煤灰：0～200份；聚合物胶粘剂：1～3份；复配外加剂：5～10份；纤维：0.9～15份。
【技术特征摘要】
1.一种免基面处理且可喷涂的抗裂防空鼓抹灰砂浆，其特征在于，以重量份计，所述抗裂防空鼓抹灰砂浆包括以下组分：通用硅酸盐水泥：100～160份；砂：680～890份；粉煤灰：0～200份；聚合物胶粘剂：1～3份；复配外加剂：5～10份；纤维：0.9～15份。2.根据权利要求1所述免基面处理且可喷涂的抗裂防空鼓抹灰砂浆，其特征在于，所述砂为天然砂、普通机制砂、尾矿砂和钒钛磁铁矿高炉渣砂中的一种或多种混合。3.根据权利要求1所述免基面处理且可喷涂的抗裂防空鼓抹灰砂浆，其特征在于，所述聚合物胶粘剂为聚乙烯醇及其共聚物胶粘剂、聚醋酸乙烯及其共聚物胶粘剂和丙烯酸脂胶粘剂中的一种或多种复合。4.根据权利要求1所述免基面处理且可喷涂的抗裂防空鼓抹灰砂浆，其特征在于，所述复配外加剂为木质素、聚丙烯酰胺、木质素磺酸盐、纤维素醚、十二烷基磺酸盐、聚羧酸盐减水剂、白糖、灰钙、石膏和淀粉醚中的两种或两种以上...