浮力传递夹具制造技术

本发明专利技术提供一种浮力传递夹具，能够抑制填充到泡沫模型的内部的型砂上浮，从而铸造成品状态良好的铸件。浮力传递夹具(1、101)具有：棒状的棒部(2)，其经由设于泡沫模型(12)而使铸型(11)的外部与空腔部(13)连通的开口部(14)从铸型(11)的外部配置至空腔部(13)的内部，并且配置在填充到空腔部(13)以及开口部(14)的硬化性的砂内；以及板状的叶片部(3)，其被设为与棒部(2)连续，且配置在型砂(15)内。

Buoyancy transfer clamp

The invention provides a buoyancy transfer clamp, which can suppress the sand floating in the interior of the foam model so as to form a casting in good condition. Buoyancy transfer fixture (1, 101) has a rod rod part (2), the model (12) is arranged through the foam and the mold (11) and the external cavity (13) an opening communicated with (14) from the mold (11) to the configuration of the external cavity (13) of the internal. And the configuration to the cavity in the filling opening (13) and (14) the hardening of sand; and the plate of the blade part (3), which is set to the Ministry with the rod (2) and continuous (15) in the configuration in the sand.

【技术实现步骤摘要】
【国外来华专利技术】浮力传递夹具
本专利技术涉及一种在铸造铸件的消失模铸造方法中使用的浮力传递夹具。
技术介绍
针对基于通常的砂型铸造的方法，提出了多种铸造尺寸精度优异的铸件的方法。例如开发了熔模铸造法(也被称作失蜡铸造)、石膏铸型铸造法、消失模铸造法等。消失模铸造法是指如下方法：在将向泡沫模型的表面涂布涂层剂而成的铸型埋入到型砂中之后，朝铸型内注入金属的熔液，使泡沫模型消失而置换成熔液，由此铸造铸件。在专利文献1中公开了根据模型的模量(模型的体积÷模型的表面积)设定铸造时的浇铸时间的消失模铸造法。在先技术文献专利文献专利文献1：日本特开2011-110577号公报
技术实现思路
然而，在通常的型腔铸造法中，在制作具有内部空间的铸件的情况下，如作为侧视剖视图的图10所示，在形成于上模21与下模22之间的空腔23内配置与铸件的内部空间相当的形状的被称作砂芯24的砂型。但是，如作为侧视剖视图的图11所示，在铸造中，砂芯24被熔液包围，沿着铅垂方向受到浮力。因此，若不存在支承砂芯24的支承部分，则砂芯24会上浮。若砂芯24上浮，则会制作出内部空间的位置偏移的铸件。因此，如作为侧视剖视图的图12所示，在砂芯24上设本文档来自技高网...

【技术保护点】
一种浮力传递夹具，其应用于消失模铸造方法，在所述消失模铸造方法中，在将向内部具有空腔部的泡沫模型的表面涂布涂层剂而成的铸型埋入型砂中之后，朝所述铸型内注入金属的熔液，使所述泡沫模型消失而置换成所述熔液，由此铸造铸件，其特征在于，所述浮力传递夹具具有：棒状的棒部，其经由设于所述泡沫模型而使所述铸型的外部与所述空腔部连通的开口部从所述铸型的外部配置至所述空腔部的内部，并且配置在填充到所述空腔部以及所述开口部的硬化性的砂内；以及板状的叶片部，其被设为与所述棒部连续，且配置在所述型砂内。

【技术特征摘要】
【国外来华专利技术】2014.12.03 JP 2014-2446301.一种浮力传递夹具，其应用于消失模铸造方法，在所述消失模铸造方法中，在将向内部具有空腔部的泡沫模型的表面涂布涂层剂而成的铸型埋入型砂中之后，朝所述铸型内注入金属的熔液，使所述泡沫模型消失而置换成所述熔液，由此铸造铸件，其特征在于，所述浮力传递夹具具有：棒状的棒部，其经由设于所述泡沫模型而使所述铸型的外部与所述空腔部连通的开口部从所述铸型的外部配置至所述空腔部的内部，并...

【专利技术属性】
技术研发人员：堤一之，
申请(专利权)人：株式会社神户制钢所，
类型：发明
国别省市：日本,JP