The invention relates to a wax free casting method for drill bits, which belongs to the technical field of casting. The casting method of the invention comprises the preparation of coating, shell preparation, roasting, smelting, pouring and post-treatment. The preparation method comprises the following steps: coating material mixing, ultrasonic vibration and mechanical agitation 8 15h, 3 5min and plasma processing, made the base paint, coating is diluted with water into a two grade paint and paint, a paint viscosity less than two coating viscosity; shell making steps: pre the wax molding surface coating paint, sandblasting and drying, and then dewaxing, made of shell body, coating the coating including the first coat and second coat, the first coat will be a rotating coating sprayed on the fusible wax surface coating will be painted second times a coating of wax type can be immersed in two grade paint out, coating paint, sandblasting and drying steps are repeated 5 times 2. The drill bit produced by the invention has the advantages of small error, accurate size and smooth surface.
【技术实现步骤摘要】
一种钻头的失蜡铸造方法
本专利技术属于铸造
,涉及一种钻头的失蜡铸造方法。
技术介绍
钻头是钻孔常用的刀具,钻头的结构通常是前端带有切削刃,刀体开有排屑槽。在使用时主要是切削端承受切削力,通过排屑槽将碎屑排出。随着科技的发展,工件对加工精度的要求越来越高,而现有的钻头采用一般的铸造方法,常存在加工精度低、误差大的问题,无法精准地加工工件。中国专利申请(CN103752907A)公开了一种空心钻钻头及其制备方法,采用机器加工、堆焊、调质回火热处理、真空镀膜防锈处理的方法制备,虽然其具有防腐、易清洁、坚固、不易变形、经久耐用的优点,但是明显地采用这种制备方法无法控制钻头的加工误差。失腊铸造法又称熔模铸造法,是指采用易熔材料制成熔模,在熔模表面包覆若干层耐火材料制成型壳,再将熔模熔化排出型壳,从而获得铸型,经高温焙烧后即可填砂浇注的铸造方案。由于熔模广泛采用蜡质材料来制造,故常称为“失蜡铸造”。失腊铸造法采用了尺寸精确、表面光滑的可熔性模,而获得了几乎无分型面的整体型壳,且无一般铸造方法中的起模、下芯、和型等工序所带来的尺寸误差,因此制备出的铸件尺寸较为精准。但是 ...
【技术保护点】
一种钻头的失蜡铸造方法,其特征在于,包括如下步骤:S1:制备涂料,将制备涂料的原材料混合,在超声振动的同时机械搅拌8‑15h,然后等离子处理3‑5min,制成基础涂料,基础涂料加水稀释制成一级涂料和二级涂料,一级涂料的粘度小于二级涂料的粘度;S2:制壳,在预成型的可熔蜡型表面涂挂涂料、喷砂并干燥,然后进行脱蜡,制成型壳坯体,所述涂挂涂料包括第一次涂挂和第二次涂挂,第一次涂挂时将S1中制得的一级涂料旋转喷涂于可熔蜡型表面,第二次涂挂时将涂有一级涂料的可熔蜡型浸入S1中制得的二级涂料中后取出,所述涂挂涂料、喷砂并干燥的步骤重复进行2‑5次;S3:焙烧,将S2中制得的型壳坯体放入 ...
【技术特征摘要】
1.一种钻头的失蜡铸造方法,其特征在于,包括如下步骤:S1:制备涂料,将制备涂料的原材料混合,在超声振动的同时机械搅拌8-15h,然后等离子处理3-5min,制成基础涂料,基础涂料加水稀释制成一级涂料和二级涂料,一级涂料的粘度小于二级涂料的粘度;S2:制壳,在预成型的可熔蜡型表面涂挂涂料、喷砂并干燥,然后进行脱蜡,制成型壳坯体,所述涂挂涂料包括第一次涂挂和第二次涂挂,第一次涂挂时将S1中制得的一级涂料旋转喷涂于可熔蜡型表面,第二次涂挂时将涂有一级涂料的可熔蜡型浸入S1中制得的二级涂料中后取出,所述涂挂涂料、喷砂并干燥的步骤重复进行2-5次;S3:焙烧,将S2中制得的型壳坯体放入焙烧炉中进行焙烧,制得型壳;S4:熔炼浇注,将制备钻头的合金熔炼成金属液体,浇注在S3中制得的型壳中,冷却后取出,即得钻头铸件;S5:后处理,对S4中制得的钻头铸件进行清理和热处理。2.根据权利要求1所述的钻头的失蜡铸造方法,其特征在于,步骤S1中所述第一次涂挂在0.05-0.20MPa的真空度下进行。3.根据权利要求1所述的钻头的失蜡铸造方法,其特征在于,步骤S1中所述旋转喷涂时的旋转速度为50-120r/min,喷涂时间15-80s。4.根据权利要求1...
【专利技术属性】
技术研发人员:练炳方,
申请(专利权)人:宁波麦克潘特电动工具有限公司,
类型:发明
国别省市:浙江,33