The invention discloses a paint elastic putty powder residue preparation and its preparation method based on weight includes the following components: waste paint slag cement particles of 60 copies, 20 copies, 4 copies of latex powder, wood fiber 6, calcite powder 10 parts. The preparation method comprises the following steps: paint slag freezing, crushing, magnetic separation, removal of impurities, grinding, adding cement, latex powder, wood fiber, calcite powder, fully mixing elastic putty powder products. The paint waste residue is replaced by one or more mixture of paint base, old powder and fly powder. The calcite powder can be replaced by talc. The invention provides an elastic putty powder which can make full use of the effective components in the paint waste residue, and has high toughness, high strength and good operation performance.
【技术实现步骤摘要】
一种基于油漆废渣制备的弹力腻子粉及其制法
本专利技术属于建筑基料生产
，更具体地说，是涉及一种基于油漆废渣制备的弹力腻子粉及其制法。
技术介绍
腻子一般主要起粘结等各种作用，腻子最常用的粘结剂是水泥和有机聚合物。水泥是粘结性好、耐久和性价比合理的粘结剂，但拉伸强度和抗裂性较差。有机聚合物可对其改性和增韧，从而提高腻子性能，形成弹力腻子粉。油漆是生活生产中常见的建筑基材，一般装修预算的油漆总会多算一点，防止一次购买不足，二次涂抹时发生色差，这就决定了常见的使用油漆的情况总会有多余的油漆废料，这些油漆废料多半干枯板结，没有发挥有效的用途，而油漆废渣中的很多成分是弹力腻子粉中主要成分，两者之间存在一定的可利用的空间。
技术实现思路
专利技术目的：本专利技术的目的就在于为解决现有技术的不足，而提供一种基于油漆废渣制备的弹力腻子粉及其制法，能够充分利用油漆废渣中的有效成分，制得韧性强度高的弹力腻子粉，变废为宝，回收利用率高。技术方案：为了实现上述专利技术目的，本专利技术所采用的技术方案为：一种基于油漆废渣制备的弹力腻子粉，包括以下重量份数的组分：废油漆渣颗粒60份，水泥20份，乳胶粉4份，木质纤维6份，方解石粉10份。一种基于油漆废渣制备的弹力腻子粉的制法，包括以下步骤：A、将油漆废渣进行冷冻，进行破碎；B、将A步骤中得到的产品进行磁选，去除杂质；C、将步骤B中得到的去除杂质后的油漆废渣进行粉碎，得到250-300目的废油漆渣颗粒；D、按比例往步骤C中得到的废油漆渣颗粒中添加水泥，乳胶粉，木质纤维，方解石粉，充分混合得到弹力腻子粉成品。所述油漆废渣由漆基、老粉及双...
【技术保护点】
一种基于油漆废渣制备的弹力腻子粉，其特征在于：所述弹力腻子粉包括以下重量份数的组分：废油漆渣颗粒60份，水泥20份，乳胶粉4份，木质纤维6份，方解石粉10份。
【技术特征摘要】
1.一种基于油漆废渣制备的弹力腻子粉，其特征在于：所述弹力腻子粉包括以下重量份数的组分：废油漆渣颗粒60份，水泥20份，乳胶粉4份，木质纤维6份，方解石粉10份。2.一种基于油漆废渣制备的弹力腻子粉的制法，其特征在于：所述制法包括以下步骤：A、将油漆废渣进行冷冻，进行破碎；B、将A步骤中得到的产品进行磁选，去除杂质；...
【专利技术属性】
技术研发人员：冒小兵，
申请(专利权)人：泰州市涂瑞装饰材料有限公司，
类型：发明
国别省市：江苏,32