To protect the environment, energy saving and emission reduction, use of industrial waste slag lithium slag as a raw material for production of white portland cement clinker, completely replace aluminum ore, limestone, silica, a small amount of fluorite, in a certain proportion, after grinding, heating and calcining, the Fe2O3 content of clinker is less than 0.45%, after cooling, can produce the production of white portland cement clinker whiteness reaches above 84 degrees. The doping amount of lithium slag according to the chemical composition of limestone, silica and fluorite proportioning calculated, the content of Fe2O3 in clinker mainly control to less than about 0.45%, after quenching, ensure the clinker whiteness reaches above 84 degrees, the other according to the chemical composition of clinker calcining need to be adjusted, the doping amount of lithium the slag is adjusted according to the blending and calcination, generally in the range of about 0.04%----15%.
【技术实现步骤摘要】
利用工业废渣锂渣作原材料生产白色硅酸盐水泥熟料
白色硅酸盐水泥熟料的生产领域。目前，生产白色硅酸盐水泥熟料的原料基本都是天然原材料，天然原材料越来越少，而工业废渣却越来越多，为减少工业废渣的环境污染，同时，也可以达到节能减排的目的，开发了一种利用工业废渣锂渣作原材料生产白色硅酸盐水泥熟料的方法。
技术介绍
四川射洪县的锂盐厂的废渣-----锂渣很多，锂渣的Fe2O3含量很低，可以作为原材料，代替铝矿，生产白色硅酸盐水泥熟料。目前生产白水泥的原料基本都是天然原材料，天然原材料越来越少，而工业废渣却越来越多，为减少工业废渣的环境污染，同时，也可以达到节能减排的目的，开发了一种利用工业废渣作原材料生产白水泥熟料的方法。
技术实现思路
利用工业废渣锂渣作为原材料，完全代替铝矿，与石灰石、硅石、少量萤石，按照一定的比例混合，经粉磨后，加热煅烧，使熟料的Fe2O3含量低于0.45%，就可以生产白度达到84度以上的白色硅酸盐水泥熟料，具体配方及结果如下：
【技术保护点】
利用工业废渣锂渣作为原材料，完全代替铝矿，与石灰石、硅石、少量萤石，按照一定的比例混合，经粉磨后，加热煅烧，使熟料的Fe2O3含量低于0.45%，就可以生产生产白度达到84度以上的白色硅酸盐水泥熟料。
【技术特征摘要】
1.利用工业废渣锂渣作为原材料，完全代替铝矿，与石灰石、硅石、少量萤石，按照一定的比例混合，经粉磨后，加热煅烧，使熟料的Fe2O3含量低于0.45%，就可以生产生产白度达到84度以上的白色硅酸...