一种蜂巢结构微孔防水透气薄膜及其制备方法技术
Honeycomb structure microporous waterproof breathable film and preparation method thereof
The invention belongs to the technical field of functional materials, in particular to a honeycomb structure microporous waterproof breathable film, and further discloses a preparation method thereof. The invention of waterproof breathable microporous film with modified polyethylene specially designed as base material, with the modification of ionic liquids, prepared with honeycomb structure waterproof breathable film, the waterproof and breathable performance has the advantage of better. The films prepared by amino acid ionic liquid modification are better than those prepared by general ionic liquid modification.
【技术实现步骤摘要】
一种蜂巢结构微孔防水透气薄膜及其制备方法
本专利技术属于功能材料
，具体涉及一种蜂巢结构微孔防水透气薄膜，并进一步公开其制备方法。
技术介绍
防水透气膜是一种新型的高分子防水材料，是一种可以让气体透过，但又能阻隔液体例如水透过的薄膜。从制作工艺上讲，防水透气膜的技术要求要比一般的防水材料高的多；同时从品质上来看，防水透气膜也具有其他防水材料所不具备的功能性特点。为了达到透气的目的，防水透气薄膜被设计制造成具有多微孔结构的独特塑料薄膜，从薄膜的横切片看，则分布着许多直径只有1-2微米的微细小孔。这样，像空气和/或水蒸气那样的气体分子很容易透过这些小孔从湿热的环境向外渗透，而外部的清新空气又不断透过这些小孔向内渗透，从而达到置换的目的，使得薄膜具有呼吸的功能；而另一方面，向液态水那样的液体分子则由于表面张力的作用难以渗透而受到阻隔，从而使这种透气薄膜具备了通风透气和防水的特征。目前，市场上已经有多种防水透气薄膜出现，比如：1)TPU防水透湿薄膜，是一种均质无孔的薄膜，采用具有亲水基团的聚氨酯弹性体TPU为主材料，利用流涎或吹塑工艺加工，但这种薄膜熔点低(120℃...
【技术保护点】
一种制备防水透薄膜的膜液组合物，其特征在于，包括质量比为10‑20：2‑5：40‑60的改性聚乙烯、离子液体以及成膜溶剂。
【技术特征摘要】
1.一种制备防水透薄膜的膜液组合物，其特征在于，包括质量比为10-20：2-5：40-60的改性聚乙烯、离子液体以及成膜溶剂。2.根据权利要求1所述的防水透薄膜的膜液组合物，其特征在于，所述改性聚乙烯、离子液体和成膜溶剂的质量比为15：3：50。3.根据权利要求1或2所述的防水透薄膜的膜液组合物，其特征在于，所述改性聚乙烯由如下重量份的组分改性制得：4.根据权利要求3所述的防水透薄膜的膜液组合物，其特征在于，所述改性聚乙烯由如下重量份的组分改性制得：5.根据权利要求3或4所述的防水透薄膜的膜液组合物，其特征在于，所述改性聚乙烯由如下方法制备：(1)常温下，取选定量的聚乙烯溶于乙醇溶液，并加入1,2-苯二甲酸单[2-[(1-氧代-2-丙烯基)氧]乙基]酯、聚对苯二甲酸乙二醇酯和羰基二咪唑混匀；(2)升温至40-50℃,向将所得混合物加入壳聚糖，充分搅拌混匀，并自然降温；(3)向降温后的混合物中加入选定量的纤维素酶混匀；(4)加入选定量的环己酮混匀，真空干燥后出料，即得。6.根据权利要求1-5任一项所述的防水透薄膜的膜液组合物，其特征在于，所述离子液体为氨基酸离子液体或咪唑类离子液体。7.根据权...
【专利技术属性】
技术研发人员：郜永红，
申请(专利权)人：南京北客纺织品有限公司，
类型：发明
国别省市：江苏,32