The invention discloses a polypropylene corrugated pipe buried Toughening Masterbatch and preparation method comprises the following raw materials by weight: superfine inorganic mineral powder 60 100; high density polyethylene resin 10 20 5 15; toughening agent; polypropylene resin 8 20 1 3; coupling agent zinc stearate; 0.5 2; 3 5 polyethylene wax. Includes the following steps: 1), raw material inspection; 2), according to the weight ratio of the raw materials; 3), mixing by kneading mixer; 4), by single screw extrusion pelletizer; 5), cooling and sieving powder, bagging test. The invention has the advantages that the invention provides a corrugated pipe masterbatch prepared by bellows material ring stiffness is more than 10, the flattening deformation test without rupture, excellent comprehensive performance, improved PP bellows on the impact of insufficient material performance.
【技术实现步骤摘要】
一种聚丙烯埋地波纹管用增韧母料及制备方法
本专利技术涉及波纹管填充母料领域，主要是一种聚丙烯埋地波纹管用增韧母料及制备方法。
技术介绍
近年来，我国的塑料管道行业得到高速的发展，应用领域不断扩大，已成为国民经济中重要的产业之一，被誉为城市中的血管，越来越受到各级政府和相关部门的关注。同时，国家相关政策引导使得塑料管道得到进一步推广应用。《国家化学建材产业十五计划和2010年发展规划纲要》、建设部《关于发布〈建设部推广应用和限制禁止使用技术〉的公告》(建设部第218号)等相关文件提出了各种塑料管道的应用领域和发展目标。聚乙烯双壁波纹管依据其优良的性能，更是得到快速发展，由于PE材料的低弹性模量，其承载压力能力相对较低，改用聚丙烯生产双壁波纹管，在相同条件下，具备更高的环刚度，但聚丙烯波纹管韧性不好，冲击强度低。有必要开发一种应用于聚丙烯双壁波纹管的增韧填充材料，来提高双壁波纹管的冲击性能。
技术实现思路
本专利技术的目的在于克服现有技术存在的不足，而提供一种聚丙烯埋地波纹管用增韧母料及制备方法。本专利技术的目的是通过如下技术方案来完成的。这种聚丙烯埋地波纹管用增韧母料，...
【技术保护点】
一种聚丙烯埋地波纹管用增韧母料，其特征在于：包括以下按重量份计的原料：超细无机矿物粉60‑100份；高密度聚乙烯树脂10‑20份；增韧剂5‑15份；聚丙烯树脂8‑20份；偶联剂1‑3份；硬脂酸锌0.5‑2份；聚乙烯蜡3‑5份。
【技术特征摘要】
1.一种聚丙烯埋地波纹管用增韧母料，其特征在于：包括以下按重量份计的原料：超细无机矿物粉60-100份；高密度聚乙烯树脂10-20份；增韧剂5-15份；聚丙烯树脂8-20份；偶联剂1-3份；硬脂酸锌0.5-2份；聚乙烯蜡3-5份。2.根据权利要求1所述的聚丙烯埋地波纹管用增韧母料，其特征在于：所述高密度聚乙烯树脂的相对密度为0.946～0.976g/cm3，熔点为130℃。3.根据权利要求1所述的聚丙烯埋地波纹管用增韧母料，其特征在于：所述超细无机矿物粉包括片状、球状、立方状和纤维状结构的粉体。4.根据权利要求1所述的聚丙烯埋地波纹管用增韧母料，其特征在于：所述超细无机矿物粉包括碳酸钙、滑石粉、高岭土、云母、石墨粉、硅灰石、硅藻土的玻璃纤维的一种或多种的组合。5.根据权利要求1...