The invention discloses a method for low-temperature sintering of wet ceramic tile whitening glaze, weight according to the raw material comprises the following components: fumed silica 15~35, rutile titanium dioxide powder 1~15, dispersant 0.3~3, antifreezing agent 0.1~1.5 and pure water 55~80. The preparation method comprises (1) by weight weighing the composition of raw materials, mixing into clean container, and mixed 0.5~3h with high-speed stirring; (2) mixing pulp after 300 mesh stainless steel screen cleaning, namely whitening glaze. The present invention by optimizing the composition of raw materials and optimization of the ratio of the whitening glaze covering ability, the fuel injection quantity is 20g/m2, 800 degrees below the burning of the wet whiteness of ceramic tiles from 38 increased to 75 degrees and the humidity of ceramic tile is not affected by the humidity effect.
【技术实现步骤摘要】
一种用于低温烧成调湿陶瓷砖的增白釉料及其制备方法
本专利技术涉及功能性建筑材料领域，尤其涉及一种低温烧成调湿陶瓷砖的增白釉料及其制备方法。
技术介绍
由于室内湿度和人类健康息息相关，为了调节室内湿度、使人生活在合适的湿度环境下，制备出了一种可以自主调节室内湿度的功能陶瓷砖。调湿功能陶瓷砖是通过表面大量纳米级的毛细微孔通过毛细凝聚和解凝作用吸附和释放水蒸气，起到主动调解室内湿度的目的。为制备出表面含有大量纳米级微孔的调湿陶瓷砖，需选用孔隙结构发达、比表面积高的粉煤灰、沸石或浮石为主要原料制备调湿陶瓷砖。粉煤灰、沸石及浮石等多孔原材料的纳米级微孔在800℃以上温度热处理下，易被生成的液相所堵塞，压重影响成品的吸湿性能；为制备出理想吸湿性能的调湿陶瓷砖，需要在低于800℃温度下对粉煤灰、沸石及浮石等多孔原材料进行低温烧成制备调湿陶瓷砖。由于制备低温烧成调湿陶瓷砖所使用的粉煤灰、沸石及浮石等原材料，含有少量难以除掉的弱磁性含铁杂质，使得烧后的调湿陶瓷砖坯体显现出铁离子的黄色调；造成调湿陶瓷砖坯体白度在40度以下，使调湿陶瓷砖的后续印花图案色彩单调，制约调湿陶瓷砖的发展应用...
【技术保护点】
一种用于低温烧成调湿陶瓷砖的增白釉料，其特征在于：按原料原料重量份计包括如下组分：气相白炭黑15~35份、金红石型二氧化钛粉体1~15份、分散剂0.3~3份、防冻剂0.1~1.5份和纯净水55~80份。
【技术特征摘要】
1.一种用于低温烧成调湿陶瓷砖的增白釉料，其特征在于：按原料原料重量份计包括如下组分：气相白炭黑15~35份、金红石型二氧化钛粉体1~15份、分散剂0.3~3份、防冻剂0.1~1.5份和纯净水55~80份。2.根据权利要求1所述的一种用于低温烧成调湿陶瓷砖的增白釉料，其特征在于：所述气相白炭黑为亲水性气相白炭黑，比表面积为100~500g/㎡。3.根据权利要求1所述的一种用于低温烧成调湿陶瓷砖的增白釉料，其特征在于：所述金红石型二氧化钛粉体平均粒径为0.05~1μm。4.根据权利要求1所述的一种用于低温烧成调湿陶瓷砖的增白釉料，其特征在于：所述分散剂选自磷酸钠、六偏磷酸钠、三聚磷酸钠、聚丙烯酸钠中的至少一种。5.根据权利要求1所述的一种用于低温烧成调湿陶瓷砖的增白釉料，其特征在...
【专利技术属性】
技术研发人员：田维，柯善军，
申请(专利权)人：佛山欧神诺陶瓷股份有限公司，
类型：发明
国别省市：广东,44