The invention discloses an environment-friendly rubber bearing, the raw materials by weight: Neoprene 90 100 copies, 45 copies of the 40 polyacrylate rubber, butyl rubber 20 filler 140 28 copies, 150 copies, 2,2 double (t-butylperoxy) propane 4 8, Zinc Oxide 0.4 0.8, accelerator M 2 6 copies, 10 copies of the 6 plasticizer, antioxidant 3 5. Environmental protection rubber bearing of the present invention, not only meet the high elasticity after curing, shock absorption function, and high dimensional stability, good fatigue resistance, with long load capacity, excellent creep resistance, while the vulcanization temperature does not decompose carcinogenic substances, there is no potential threat to human health.
【技术实现步骤摘要】
一种环保隔震橡胶支座
本专利技术涉及橡胶
，尤其涉及一种环保隔震橡胶支座。
技术介绍
环保隔震橡胶支座是一种由多层橡胶与薄钢板镶嵌、粘合、硫化形成的桥梁支座产品。该类型的橡胶支座有足够的竖向刚度以承受垂直荷载，能将上部构造的压力可靠地传递给墩台；此外，有良好的弹性以适应梁端的转动，并具有较大的剪切变形以满足上部构造的水平位移。目前国内在用的环保隔震橡胶支座还存在废弃后污染环境，而且抗疲劳性差，抗蠕变性能满足不了需求，亟待解决。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种环保隔震橡胶支座，硫化后不仅弹性极高，满足减震功能，而且尺寸稳定性极高，抗疲劳性好，具有长期的负载能力，抗蠕变性能极好，同时硫化温度下不会分解出致癌物质，对人类健康不存在潜在威胁。本专利技术提出的一种环保隔震橡胶支座，其原料按重量份包括：氯丁橡胶90-100份，聚丙烯酸酯橡胶40-45份，丁基橡胶20-28份，填充料140-150份，2,2-双-(叔丁基过氧)丙烷4-8份，氧化锌0.4-0.8份，硫化促进剂M2-6份，增塑剂6-10份，抗氧剂3-5份。优选地，增塑剂按重量份包括...
【技术保护点】
一种环保隔震橡胶支座，其特征在于，其原料按重量份包括：氯丁橡胶90‑100份，聚丙烯酸酯橡胶40‑45份，丁基橡胶20‑28份，填充料140‑150份，2,2‑双‑(叔丁基过氧)丙烷4‑8份，氧化锌0.4‑0.8份，硫化促进剂M 2‑6份，增塑剂6‑10份，抗氧剂3‑5份。
【技术特征摘要】
1.一种环保隔震橡胶支座，其特征在于，其原料按重量份包括：氯丁橡胶90-100份，聚丙烯酸酯橡胶40-45份，丁基橡胶20-28份，填充料140-150份，2,2-双-(叔丁基过氧)丙烷4-8份，氧化锌0.4-0.8份，硫化促进剂M2-6份，增塑剂6-10份，抗氧剂3-5份。2.根据权利要求1所述环保隔震橡胶支座，其特征在于，增塑剂按重量份包括：邻苯二甲酸二异辛酯2-4份，芳香烃油2-4份，环烷烃油2-4份。3.根据权利要求1或2所述环保隔震橡胶支座，其特征在于，填充料按重量份包括：纤维复合物50-70份，纳米硬质沥青10-20份，白炭黑50-70份，石墨10-18份。4.根据权利要求1-3任一项所述环保隔震橡胶支座，其特征在于，纤维复合物采用如下工艺制备：将花生蛋白粉、水搅拌，调节体系pH至7.1-7.4，加入胰蛋白酶酶解，灭活，调节体系pH至中性，加入钛酸酯偶联剂、剑麻纤维、兔毛纤维搅拌均匀，加入聚乙烯醇、聚乳酸混合均匀，升温，继续搅拌，过滤，洗涤，干燥，粉碎得到纤维复合物。5.根...
【专利技术属性】
技术研发人员：潘海洋，刘梅霞，王成，
申请(专利权)人：合肥绿洁环保科技有限公司，
类型：发明
国别省市：安徽,34