本发明专利技术公开了一种基于双金属氧化物无溶剂制备Co‑MOF材料的方法，该方法是含钴双金属氧化物与配体化合物研磨混合后，置于密封釜内，在80～300℃温度下反应，即得比表面大，且同时具有介孔和微孔的Co‑MOF材料，该方法操作简单、周期短，产率高，提供了一种新的MOF材料制备途径，大大降低了MOF材料的生产成本，有利于工业化生产。

Method of cobalt containing double metal oxide solvent-free preparation of Co based on MOF material

The invention discloses a method for double metal oxide solvent-free preparation of Co based on MOF material, the method of double metal oxide containing cobalt and compounds mixed after grinding, is placed in a sealed reaction kettle, at 80 to 300 DEG, which have large surface area, Co MOF and materials with dielectric pores and micropores, the method has the advantages of simple operation, short cycle, high yield, a new preparation method of MOF material is provided, greatly reduces the production cost of MOF materials, suitable for industrial production.

【技术实现步骤摘要】
基于含钴双金属氧化物无溶剂制备Co-MOF材料的方法
本专利技术涉及一种Co-MOF材料的制备方法，特别涉及一种通过含钴双金属氧化物快速、便捷，在无溶剂条件下制备MOF材料的方法；属于MOF材料制备

技术介绍
金属有机骨架结构材料(Metal-OrganicFrameworks,MOFs)是由金属离子与多官能团有机配体配位而成的一种具有高比表面积、吸附性能好、热稳定性好的新型多孔材料。由于金属离子和有机配体种类的多样化，其具有大的比表面积、孔隙率、结构多样等特点，在气体吸附、储存以及催化等领域具有很好的发展前景。因此，材料的制备及性能研究成为当前最具吸引力的课题之一。由于含钴类物质的高催化活性及在储能中的一些潜在应用，Co-MOF(ZIF-67)被广泛的研究了。目前制备Co-MOF方法大多是根据传统的水热法或者溶剂法，一般以N,N-二甲基甲酰胺、甲醇或者水做溶剂，反应完之后在离心分离。这些方法大都反应复杂，需要分几步完成，且生成的Co-MOF的形貌比较单一，不利于调控。由于反应的前驱体Co(NO3)3中只有一种金属离子，导致Co-MOF中通常只含有一种金属阳离子，这极大的限本文档来自技高网...

【技术保护点】
基于含钴双金属氧化物无溶剂制备Co‑MOF材料的方法，其特征在于：含钴双金属氧化物与配体化合物研磨混合后，置于密封釜内，在80～300℃温度下反应，即得。

【技术特征摘要】
1.基于含钴双金属氧化物无溶剂制备Co-MOF材料的方法，其特征在于：含钴双金属氧化物与配体化合物研磨混合后，置于密封釜内，在80～300℃温度下反应，即得。2.根据权利要求1所述的基于含钴双金属氧化物无溶剂制备Co-MOF材料的方法，其特征在于：所述含钴双金属氧化物包括CoSnO3、CoSb2O4、CoFe2O4、CoMnO3、CoMoO4、CoSn2O4中至少一种。3.根据权利要求1所述的基于含钴离双金属氧化物无溶剂制备Co-MOF材料的方法，其特征在于：所述配体化合物包括对苯二甲酸、均苯三甲酸、2-甲基咪唑中的至少一种。4.根据权利要求1～3任一项所述的基于含钴双金属氧化物无溶剂制备...