The invention of a method for preparing inorganic crosslinking modified natural polymer polyacrylic acid superabsorbent resin, the method comprises: dissolving sodium silicate in sodium hydroxide solution, and then under stirring, in turn, acrylic acid sodium hydroxide solution of sodium silicate, (modified) natural polymer solution is added to the reactor. The system of constant temperature to a certain temperature, adding initiator system began to gel, reaction time, the gel is dried, crushed and sieved to obtain granular products. The preparation process needs no nitrogen protection, and the method is simple and easy to operate. The structure of the superabsorbent resin is a sodium silicate crosslinked (modified) natural polymer modified partially neutralized polyacrylic acid. This super absorbent resin has both high water absorption and easy degradation.
【技术实现步骤摘要】
一种无机物交联制备天然高分子改性聚丙烯酸高吸水性树脂的方法
本专利技术涉及到一种高吸水性树脂的制备方法，尤其是无机物作为交联剂、天然大分子改性的高吸水性树脂的制备。
技术介绍
高吸水性树脂为轻度交联的高分子，其分子链上含有亲水基团如羟基、羧基、酰胺基等，吸水能力强，能吸收自身重量几百倍甚至上千倍的纯水和数十倍的盐水，并且保水能力强，加压下也不脱水，广泛应用于农业、林业、卫生产品、废水处理等方面。聚丙烯酸系高吸水性树脂以其高吸水率、高吸水速度等优点成为高吸水性树脂中最重要的品种之一，但传统的聚丙烯酸（盐）高吸水性树脂，常采用有机交联剂，其交联网络难以被土壤中的微生物和细菌所分解，属于非生物降解性聚合物，在大量废弃后势必带来巨大的环境污染问题。天然聚合物（如淀粉、纤维素、壳聚糖、海藻酸钠）一般为可生物降解材料，它能提供高浓度、高活性的微生物及其生长环境，这些天然高分子与丙烯酸共聚后，可以使整个高分子网络具有一定的生物降解性。另一方面，硅酸钠价廉易得，它以硅氧四面体作为基本结构单元组成硅酸根阴离子，在酸性水溶液中，其表面的Si-OH可以与丙烯酸-COOH发生反应，使线型...
【技术保护点】
一种无机物交联制备天然高分子改性聚丙烯酸高吸水性树脂的方法，其特征在于，依次包含下述步骤：（1）一定质量的硅酸钠溶解于氢氧化钠溶液中；（2）安装好反应设备，依次将一定量的丙烯酸、硅酸钠碱溶液、（改性的）天然高分子溶液加入到反应溶器中；（3）当体系的温度为20~50℃时，加入引发剂，反应0.5~4h后，烘干、粉碎、过筛得颗粒状产品。
【技术特征摘要】
1.一种无机物交联制备天然高分子改性聚丙烯酸高吸水性树脂的方法，其特征在于，依次包含下述步骤：（1）一定质量的硅酸钠溶解于氢氧化钠溶液中；（2）安装好反应设备，依次将一定量的丙烯酸、硅酸钠碱溶液、（改性的）天然高分子溶液加入到反应溶器中；（3）当体系的温度为20~50℃时，加入引发剂，反应0.5~4h后，烘干、粉碎、过筛得颗粒状产品。2.如权利1中所述无机物交联制备天然高分子改性聚丙烯酸高...