一种基于CSP工艺的无取向硅钢连退入口切尾卷的方法技术

本发明专利技术公开了一种基于CSP工艺的无取向硅钢连退入口切尾卷的方法，其在酸轧出口分卷时根据硅钢退火线反馈的预设长度在焊缝前进行预先剪切，把上一卷尾部超差部分卷在下一卷的卷心部位，然后在入口通过甩尾卷将超差部分切除。采用上述方法不仅解决了钢卷外圈超出部分无法切除的问题，同时破解了内圈尾卷过小无法下卷的难题。采用该方法不但可以节省超差部分通过硅钢及重卷线时的加工费，还可以大幅提高硅钢及重卷产量。

Method for cutting tail roll of non oriented silicon steel continuous entry and exit based on CSP process

The invention discloses a non oriented silicon steel CSP process based on continuous annealing method cut tail roll entrance, the export volume in acid rolling according to the silicon steel annealing line feedback in advance before the preset length weld shear, put a roll of tail outoftolerance part volume in the next volume of the iceberg site, and then in the entrance the tail volume will outoftolerance part resection. Using the above method not only solves the outer coil excess unresectable, and solved the problem of too small to the volume of the inner tail. This method can not only save the ultra poor parts, but also increase the output of silicon steel and heavy coil greatly.

【技术实现步骤摘要】
一种基于CSP工艺的无取向硅钢连退入口切尾卷的方法
本专利技术涉及金属加工
，特别是涉及一种基于CSP工艺的无取向硅钢连退入口切尾卷的方法。
技术介绍
基于CSP工艺的无取向硅钢的典型生产工艺为：转炉炼钢、RH、CSP连铸连轧、冷连轧、连续退火涂层、重分卷。实际生产过程中，CSP热连轧时头尾处于失张状态，导致带钢头尾厚度超差较为严重，冷连轧后厚度公差仍无法满足硅钢标准要求；另外，在硅钢热轧卷冷却过程中内外圈冷速过快，导致晶粒细小，经退火后头尾铁损值较高，超出标准要求。从减少过程加工费的角度出发，超差部分越早切除越有利。CSP热连轧、冷连轧、连续退火涂层出口段生产节奏快，无法将超差部分切除。重分卷为断续生产模式，便于完成超差部分切除，典型超差部分切除为重分卷切除，这种处理方式不但造成超差部分过连续退火涂层机组及重分卷机组时加工费浪费，同时使重分卷分切量从正常的一分三增加到了一分五，严重影响了重卷成品卷的产量。
技术实现思路
为了解决以上技术问题，本专利技术提供一种基于CSP工艺的无取向硅钢连退入口切尾卷的方法。本专利技术提供一种基于CSP工艺的无取向硅钢连退入口切尾卷的方法，其是在酸本文档来自技高网...

【技术保护点】
一种基于CSP工艺的无取向硅钢连退入口切尾卷的方法，其特征在于，在酸轧出口分卷时根据硅钢退火线反馈的预设长度在焊缝前进行预先剪切，把上一卷尾部超差部分卷在下一卷的卷心部位，然后在入口通过甩尾卷将超差部分切除。

【技术特征摘要】
1.一种基于CSP工艺的无取向硅钢连退入口切尾卷的方法，其特征在于，在酸轧出口分卷时根据硅钢退火线反馈的预设长度在焊缝前进行预先剪切，把上一卷尾部超差部分卷在下一卷的卷心部位，然后在入口通过甩尾卷将超差部分切除。2.根据权利要求1所述的基于CSP工艺的无取向硅钢连退入口切尾卷的方法，其特征在于，...

【专利技术属性】
技术研发人员：詹卢刚，孙丽钢，
申请(专利权)人：内蒙古包钢钢联股份有限公司，
类型：发明
国别省市：内蒙古,15