The invention provides a diamond wire preparation process, belonging to the mechanical technical field. It solves the problems existing in the existing technology. The preparation process of the diamond line comprises the following steps: A, line: by electroplating process existing in metal blank layer, steel wire surface plating a layer of uniform thickness and easy welding; B, pretreatment: the blank surface coated with a layer of uniform flux; C, molding: in a blank surface flux the connection of diamond powder; D, cooling: 2 - 5 hours after natural cooling solidification in the natural environment, get the diamond wire; E, wire: the diamond wire prepared orderly winding roller online. The process is easy to implement, and the product quality is relatively high.
【技术实现步骤摘要】
金刚石线的制备工艺
本专利技术属于机械
，涉及一种金刚石线的制备工艺。
技术介绍
现有的通过金刚石线主要有两种：电镀金刚石线和树脂金刚石线。电镀金刚石线是在钢丝线的表面电镀金刚石粉末，虽然它个性性能指标优异，但是，其成本成本比较高。树脂金刚石主要是讲微粉和树脂混合，它的缺点是粘结牢固不够，切割过程中会出现树脂脱落的情况，其稳定性不高。中国专利其公开号CN102935420A公开了一种金刚石线锯植砂方法及系统，所述金刚石线锯植砂方法包括：1)使金刚石颗粒和树脂粘合剂混合，形成均匀的混合物；2)将所述混合物均匀涂覆在芯线表面；3)对芯线进行固化处理。通过上述提供的金刚石线锯植砂方法可以使得金刚石颗粒在芯线表面均匀分布，同时可控制金刚石颗粒的露出率，从而保障了金刚石线锯的切割精度和切割效率，并延长了金刚石线锯的使用寿命。可以看出，上述专利的金刚石线锯植砂方法制作的还是树脂金刚石，其金刚石线还是存在着产品稳定性不高的问题。
技术实现思路
本专利技术的目的是针对现有技术存在的上述问题，提供一种能提高金刚石线稳定性以及易于实施的金刚石线的制备工艺。本专利技术的目的可通过下列...
【技术保护点】
一种金刚石线的制备工艺，该工艺包括以下步骤：A、放线：通过现有的电镀工艺在钢丝表面电镀一层厚度均匀且易于焊接的金属层，得到毛坯；B、预处理：在毛坯表面均匀涂覆一层助焊剂；C、成型：在具有助焊剂的毛坯表面连接金刚石微粉；D、冷却：在自然环境下经3—60秒自然冷却凝固成型，得到金刚石线；E、收线：将制备的金刚石线有序的绕卷在线辊上。
【技术特征摘要】
1.一种金刚石线的制备工艺，该工艺包括以下步骤：A、放线：通过现有的电镀工艺在钢丝表面电镀一层厚度均匀且易于焊接的金属层，得到毛坯；B、预处理：在毛坯表面均匀涂覆一层助焊剂；C、成型：在具有助焊剂的毛坯表面连接金刚石微粉；D、冷却：在自然环境下经3—60秒自然冷却凝固成型，得到金刚石线；E、收线：将制备的金刚石线有序的绕卷在线辊上。2.根据权利要求1所述的金刚石线的制备工艺，其特征在于，所述的步骤C中待喷涂件经过一成型模具，成型模具上具有贯穿的通孔，通孔的孔径略大于待喷涂件外径。3.根据权利要求1所述的金刚石线的制备工艺，其特征在于，所述步骤C中通过成型模具,将焊锡液均匀涂抹在钢线表面,制成待喷涂件,在焊锡液凝固之前,将镀有易焊接金属的金刚石微粉,通过不同角度的喷嘴,喷在待涂件表面。4.根据权利要求1所述的金刚石线的制备工艺，其特征在于，所述步骤C中在成型模中将融...