片状Co‑MOF纳米材料的制备方法及其在电催化中的应用，涉及电解水、燃料电池和金属‑空气电池等技术领域，本发明专利技术的片状Co‑MOF电极材料是由简单水热法制备而成，采用的原材料环保、成本低，工艺简单，易于操作控制，适于连续化大规模生产，制备过程绿色环保。经实验证实，这种Co‑MOF纳米材料具有片状结构，由于其高的比表面积、优良的电导率等优异性能，可用于电催化。

Application of method of preparation of flake Co MOF nano material and in electrocatalysis

Preparation method of Co flake MOF nano material and its application in electrocatalysis, relates to the technical field of electrolysis of water, fuel cell and metal air battery, flake Co MOF electrode material of the invention is by simple hydrothermal preparation and use of raw materials, environmental protection, low cost and simple process. Easy to control, and is suitable for large-scale production, preparation process is green. The experiment confirmed that the Co MOF nano materials with lamellar structure, due to its high surface area, excellent conductivity and excellent performance, can be used in electrocatalysis.

【技术实现步骤摘要】
片状Co-MOF纳米材料的制备方法及其在电催化中的应用
本专利技术涉及电解水、燃料电池和金属-空气电池等
，特别是其电极材料的制备技术。
技术介绍
化石燃料的过渡消耗及其所引起的环境污染问题，迫使着人们不断寻求清洁可再生新能源。因为通过电催化反应直接将化学能转换成电能，具有高转换效率、低噪声和低排放等优点。燃料电池和金属空气电池是目前很具有应用前景的新型能源装置。传统上使用金属氧化物（例如RuO2和IrO2）和贵金属（例如Pt）来加速析氧反应（OER）和氧还原反应（ORR），然而，这些贵金属基催化剂通常具有高成本，低选择性，差的稳定性以及对环境不利的影响。因此，开发廉价和高效的非贵重金属材料用于电催化，以代替昂贵的基于Ir和Ru的化合物，人们已经作出了巨大的努力。钴（Co）已经成为设计和制造坚固的最常见的非贵重元素之一和高效的OER催化剂。金属有机骨架材料（Metal-organicframeworks,MOFs）是一种由金属离子和有机配体通过配位键组装的无机-有机杂化功能材料，是近十几年来发展最为迅速的一种新型多孔材料，具有三维的孔结构，一般以金属离子为连接点，有机配位体支撑本文档来自技高网...

【技术保护点】
片状Co‑MOF纳米材料的制备方法，其特征在于包括以下步骤：1）将二价钴盐溶于去离子水中，制得二价钴盐溶液；将对苯二甲酸溶于二甲基甲酰胺与乙醇的混合溶液中，制得对苯二甲酸的DMF/C

【技术特征摘要】
1.片状Co-MOF纳米材料的制备方法，其特征在于包括以下步骤：1）将二价钴盐溶于去离子水中，制得二价钴盐溶液；将对苯二甲酸溶于二甲基甲酰胺与乙醇的混合溶液中，制得对苯二甲酸的DMF/C2H5OH溶液；2）将所述二价钴盐溶液与对苯二甲酸的DMF/C2H5OH溶液混合，再加入聚乙烯吡咯烷酮进行水热反应，得到沉淀物；3）将沉淀物以水和乙醇洗涤后干燥，即得片状Co-MOF纳米材料。2.根据权利要求1所述的制备方法，其特征在于所述二价钴盐为Co(NO3)2•6H2O、CoSO4•H2O或Co(CH3COO)2•4H2O。3.根据权利要求1所述的制...

【专利技术属性】
技术研发人员：庞欢，徐玉霞，郑莎莎，吴平，詹婧逸，
申请(专利权)人：扬州大学，
类型：发明
国别省市：江苏,32