The invention discloses a preparation method of ferromolybdenum smelting charge, the method comprises the following steps: A, the binder components in parts by weight of 30-50 copies of copies of the 40-60 molybdenum powder, iron powder, 10-15 parts of the toner, 8-10 uniform mixing; B, mixing the materials after moistening or pressed into blocks C, the ball; sintering block or ball sintering machine pressed; D, after sintering cooling the ferromolybdenum smelting furnace. The invention relates to a preparation method of molybdenum smelting charge, by optimizing the ratio of raw materials can make the sintering burden easier, lower energy consumption, and no pollution, not only conducive to energy conservation and environmental protection, but also effectively reduces the production cost, and improve the quality of products.
【技术实现步骤摘要】
一种钼铁冶炼炉料制备方法
本专利技术涉及一种钼铁冶炼工艺,特别是涉及一种钼铁冶炼炉料制备方法。
技术介绍
钼铁是重要的冶金、化工添加剂,钼铁的制备其炉料又显得尤为关键,炉料的制备效果直接影响钼铁冶炼的金属化率和成本品质,而目前的工艺还存在诸多的不足,如能耗高等。
技术实现思路
本专利技术所要解决的技术问题是提供一种工艺简单、节能环保的钼铁冶炼炉料制备方法。为了解决上述技术问题,本专利技术采用如下技术方案:一种钼铁冶炼炉料制备方法,包括以下步骤:A、将按质量份数计的30-50份的钼矿粉、40-60份的铁粉、10-15份的碳粉、8-10的粘结剂均匀混合;B、将混合后的物料加水湿润后压制成块或球;C、将压制成的块或球置于烧结机上进行烧结;D、烧结后进行冷却即得钼铁冶炼炉料。作为优选,所述步骤A中钼矿粉的粒径为0.2-0.6毫米。作为优选,所述步骤B中块或球的质量为5-10克。与现有技术相比,本专利技术一种钼铁冶炼炉料制备方法,通过优化原料配比可使炉料的烧结更为容易,能耗更低,且无污染物产生,不仅有利于节能环保,还有效地降低了生产成本,同时提高了产品的品质。具体实施方式本说明书中公开的所有特征,或公开的所有方法或过程中的步骤,除了互相排斥的特征和/或步骤以外,均可以以任何方式组合。本说明书中公开的任一特征,除非特别叙述,均可被其他等效或具有类似目的的替代特征加以替换。即,除非特别叙述,每个特征只是一系列等效或类似特征中的一个例子而已。实施例1:本专利技术一种钼铁冶炼炉料制备方法,包括以下步骤:A、将按质量份数计的30份的钼矿粉、40份的铁粉、10份的碳粉、8的粘结剂均 ...
【技术保护点】
一种钼铁冶炼炉料制备方法,其特征在于,包括以下步骤:A、将按质量份数计的30‑50份的钼矿粉、40‑60份的铁粉、10‑15份的碳粉、8‑10的粘结剂均匀混合;B、将混合后的物料加水湿润后压制成块或球;C、将压制成的块或球置于烧结机上进行烧结;D、烧结后进行冷却即得钼铁冶炼炉料。
【技术特征摘要】
1.一种钼铁冶炼炉料制备方法,其特征在于,包括以下步骤:A、将按质量份数计的30-50份的钼矿粉、40-60份的铁粉、10-15份的碳粉、8-10的粘结剂均匀混合;B、将混合后的物料加水湿润后压制成块或球;C、将压制成的块或球置于烧结机上进行烧结...