The invention discloses a process for production of molybdenum electric heating method, the process comprises the following steps: A, molybdenite roasting oxidation of molybdenum; B, oxidation of molybdenum ore after crushing, adding iron oxide powder and mixed evenly; C, to mixed powder with binder pressed block D, block blank; in high temperature heating furnace for smelting FERRO MOLYBDENUM can be obtained. The invention relates to a process for production of molybdenum by electric heating, the molybdenite roasting pulverizing and iron oxide powder, toner evenly mixed into blocks obtained by the high temperature electric furnace smelting ferromolybdenum, not only has the advantages of simple equipment, short preparation cycle, and the operation difficulty is low, no environmental pollution, low production cost.
【技术实现步骤摘要】
一种电热法生产钼铁的工艺
本专利技术涉及一种冶金方法，特别是涉及一种钼铁生产的工艺。
技术介绍
钼铁合金目前主要铝热法进行制备，其热源主要是铝和硅，其所需设备不仅复杂而且造价高，反应产物对环境的污染也较大，因此其严重不符合节能环保的生产理念。
技术实现思路
本专利技术所要解决的技术问题是提供一种所需设备简单且无污染的电热法生产钼铁的工艺。为了解决上述技术问题，本专利技术采用如下技术方案：一种电热法生产钼铁的工艺，包括以下步骤：A、将辉钼矿进行焙烧得到氧化钼矿；B、将氧化钼矿粉碎后加入氧化铁粉、碳粉并混合均匀；C、向混合粉末中加入粘结剂再压制成块；D、将块坯放入高温电热炉中进行熔炼即可得到钼铁。作为优选，所述步骤B中氧化钼矿粉、氧化铁粉、碳粉的质量比为3:1:1或4:1:1。作为优选，所述步骤D中采用的电热炉为等离子电热炉。与现有技术相比，本专利技术一种电热法生产钼铁的工艺，通过将辉钼矿焙烧后制粉并与氧化铁粉、碳粉均匀混合后制成块再通过高温电热炉冶炼得到钼铁，不仅设备简单，制备工艺周期较短，而且操作难度低，环保无污染，生产制造成本低。具体实施方式本说明书中公开的所有特征，或公开的所有方法或过程中的步骤，除了互相排斥的特征和/或步骤以外，均可以以任何方式组合。本说明书中公开的任一特征，除非特别叙述，均可被其他等效或具有类似目的的替代特征加以替换。即，除非特别叙述，每个特征只是一系列等效或类似特征中的一个例子而已。实施例1：本专利技术一种电热法生产钼铁的工艺，包括以下步骤：A、将辉钼矿进行焙烧得到氧化钼矿；B、将氧化钼矿粉碎后加入氧化铁粉、碳粉并混合均匀，所述氧化钼...
【技术保护点】
一种电热法生产钼铁的工艺，其特征在于，包括以下步骤：A、将辉钼矿进行焙烧得到氧化钼矿；B、将氧化钼矿粉碎后加入氧化铁粉、碳粉并混合均匀；C、向混合粉末中加入粘结剂再压制成块；D、将块坯放入高温电热炉中进行熔炼即可得到钼铁。
【技术特征摘要】
1.一种电热法生产钼铁的工艺，其特征在于，包括以下步骤：A、将辉钼矿进行焙烧得到氧化钼矿；B、将氧化钼矿粉碎后加入氧化铁粉、碳粉并混合均匀；C、向混合粉末中加入粘结剂再压制成块；D、将块坯放入高温电热炉中进行熔炼即可得到钼铁。2....
【专利技术属性】
技术研发人员：李成，
申请(专利权)人：四川省东宇信息技术有限责任公司，
类型：发明
国别省市：四川,51