Method for preparing bagasse carbon material by hydrothermal method and application thereof
The invention relates to a carbon material prepared from bagasse and an application field thereof. The juice of bagasse residual collection cleaning, drying, crushing, sieving, by hydrothermal carbonization method, in addition with the carbonization water heat medium oxygen acid after washing and drying are multifunctional and high adsorption carbon materials - bagasse hydrothermal carbon. The preparation process of raw materials, low cost, simple operation, friendly environment; the prepared surface loose porous carbon materials, and rich in oxygen-containing functional groups or have large surface area, can be used for efficient treatment of dye containing wastewater and heavy metals or sugar in sugar industry decolorization, achieve a green sugar process the good economic benefit and social benefit and environmental benefit.
【技术实现步骤摘要】
一种水热法制备甘蔗渣炭材料的方法及应用
本专利技术涉及废弃生物质制备炭材料领域，尤其涉及一种水热法制备甘蔗渣炭材料的方法及应用。
技术介绍
中国是世界第三大甘蔗种植国，甘蔗属于我国南方主要的农作物之一，主要应用于制糖工业。甘蔗榨汁后有近四分之一的部分形成甘蔗渣，近年来我国蔗糖年产量在1000～1100万吨左右，由此产生大量的甘蔗渣副产物。目前，甘蔗渣主要用于燃烧供能、造纸等途径，其资源化综合利用率低，并且约有700多万吨未被再利用的甘蔗渣被废弃于田野或是焚烧处理，造成了严重的环境污染和天然生物质资源的极大浪费。因此，有效利用甘蔗渣作为原料，发展环境友好型的高附加值产品具有环境和经济的双重效益。活性炭孔隙结构发达、比表面积大，它具有化学稳定性好、吸附能力强、便于再生利用等优点，是一种重要的吸附材料，被广泛应用于水处理、食品工业、化工等领域。随着工业发展及环境保护要求的提高，全球活性炭的供、需逐年增加，我国近几年对活性炭的进出口量也出现迅猛的增长势头。目前制备活性炭的原料主要来源于煤炭和木材、椰子壳等农林副产品。其中，甘蔗渣由于具有含碳量高、原料来源集中且丰富、价格低...
【技术保护点】
一种水热法制备甘蔗渣炭材料的方法，其特征在于包括以下步骤：1)粉碎甘蔗渣；2)将甘蔗渣与0‑5v％含氧酸进行混合，并放入水热反应釜内进行水热碳化反应，其中水热碳化反应温度为200～280℃，反应时间为8‑12h；3)过滤收集反应后的固体，洗涤并干燥后得到所述炭材料。
【技术特征摘要】
1.一种水热法制备甘蔗渣炭材料的方法，其特征在于包括以下步骤：1)粉碎甘蔗渣；2)将甘蔗渣与0-5v％含氧酸进行混合，并放入水热反应釜内进行水热碳化反应，其中水热碳化反应温度为200～280℃，反应时间为8-12h；3)过滤收集反应后的固体，洗涤并干燥后得到所述炭材料。2.如权利要求1所述的水热法制备甘蔗渣炭材料的方法，其特征在于：所述步骤2)中，甘蔗渣与含氧酸固液质量比为1:15～25。3.如权利要求1所述的水热法制备甘蔗渣炭材料的方法，其特征在于：所述步骤2)中，所述含氧酸至少包括丙烯酸或磷酸中的一种。4...