一种介孔碳材料的制备方法技术
Preparation method of mesoporous carbon material
The invention relates to a preparation method of a mesoporous carbon material, a carbon material preparation and application technology; compared with the prior art, the invention has significantly advanced, with small organic molecules as the carbon source, reducing agent sodium potassium alloy, toluene as solvent, stirring force in at room temperature, into the reaction solution, by filtration, washing and vacuum drying, made of mesoporous carbon materials, the preparation method of advanced technology, accurate data accurate, fast in preparation, without high-temperature calcination, product of black powder, the mesoporous pore structure, high product yield, up to 75.6%, can be matched with various chemical preparation method of mesoporous carbon materials is very ideal.
【技术实现步骤摘要】
一种介孔碳材料的制备方法
本专利技术涉及一种介孔碳材料的制备方法，属碳材料的制备及应用的
技术介绍
介孔碳材料具有良好的结构可调性和稳定性，是其他材料无法比拟的，介孔碳材料具有较高的比表面积和较大的孔体积，在吸附、催化、光学、电学领域得到了广泛应用。介孔碳材料的合成方法和过程会直接影响材料的结构特征与性能，例如模板剂和前驱体的选择是决定性的影响因素，反应温度、溶剂、反应物的比例、反应体系的pH值、焙烧温度也会有重要的影响。模板剂是合成介孔碳材料的基本组成部分，有机前驱体与模板剂通过自组装或者纳米浇铸的方法形成介孔结构。模板剂的结构和种类将影响介孔碳材料的孔道结构，因此模板剂的选择和使用是十分重要的。以有机小分子或者聚合物作为前驱体合成碳材料的过程中，大都需要在惰性气氛下高温焙烧碳化，由于选用的化学物质不同，合成参数的不同，合成过程的差异，碳化温度从600℃到1800℃，所得碳材料化学物理性能差别较大，很难满足合成物质的要求，使此类材料的应用受到了很大的局限性。
技术实现思路
为解决上述问题，本专利技术的目的是采用一种新的金属还原合成法，以钠钾合金作金属还原剂...
【技术保护点】
一种介孔碳材料的制备方法，其特征在于，包括步骤如下：是以有机小分子为碳源，以钠钾合金为还原剂，以甲苯为溶剂，在氮气保护条件下，经在室温下磁力搅拌反应10～12h，制成反应溶液，经抽滤、洗涤、真空干燥，制成介孔碳材料。
【技术特征摘要】
1.一种介孔碳材料的制备方法，其特征在于，包括步骤如下：是以有机小分子为碳源，以钠钾合金为还原剂，以甲苯为溶剂，在氮气保护条件下，经在室温下磁力搅拌反应10～12h，制成反应溶液，经抽滤、洗涤、真空干燥，制成介孔碳材料。2.根据权利要求1所述的一种介孔碳材料的制备方法，其特征在于，所述钠钾合金的配制过程为：按照质量比为1：4的比例称取金属钠和金属钾，搅拌1min，成钠钾合金。3.根据权利要求1所述的一种介孔碳材料的制备方法，其特征在于，所述磁力搅拌反应的具体步骤为：①配制混合反应混合物按照质量比为1.2：1.8称取四氯化碳和钠钾合金置于圆底烧瓶中，再向其中加入甲苯200mL～300mL，成混合反应溶液；②开启磁力搅拌，搅拌时间10h，混合反应溶液进行反应，反应方程式如下：CCl4+4Na＝4NaCl+CCCl4+4K＝4KCl+C③反应完成后，停止搅拌，加入乙醇100～150mL。4.根据权利要求1所述的一...
【专利技术属性】
技术研发人员：汤兑海，赵震，朱君江，张文婷，
申请(专利权)人：沈阳师范大学，
类型：发明