The invention discloses a method for preparing hydrogenated rosin pentaerythritol ester, the method is: pentaerythritol rosin and turpentine added into a reaction kettle, adding catalyst and vegetable oil, introducing hydrogen, hydrogen pressure of 5 35 MPa, 80 temperature 300 degrees, 1 hydrogenation reaction for 10 hours, evaporated in vacuum to obtain a hydrogenated rosin pentaerythritol ester. Among them, the catalyst is palladium carbon, or palladium three, oxidation two aluminum, or nickel, vegetable oil. The quality of rosin, pentaerythritol ester, turpentine, vegetable oil and catalyst is 1:1 to 5:0.05 ~ 0.3:0.01 to 0.1. The product has the advantages of light color and good stability, and is applied to high-grade hot melt adhesive, pressure-sensitive adhesive, coating and the like.
【技术实现步骤摘要】
一种氢化松香季戊四醇酯的制备方法
本专利技术属于有机化学
特别涉及一种氢化松香季戊四醇酯的制备方法。
技术介绍
松香酸(Rosinacids)为二萜不饱和树脂酸，具有三环骨架结构，含有2个双键和1个羧基，具有较大分子体积位阻，经酯化、氢化等改性后，性能更佳。目前，各种改性松香树脂广泛应用于涂料、油墨、橡胶、造纸、食品添加剂及交联剂等领域。氢化松香季戊四醇酯简称PEHR，分子量850～890。淡黄色粒状或片状透明固体。软化点97～102℃。玻璃化温度Tg57℃，黏度620mPa·S(160℃)、3000mPa·S(140℃)。溶于甲苯、醋酸乙酯、丙酮、溶剂汽油、松节油等，不溶于乙醇、水。具有良好的粘接性，更好的耐老化性。用作溶剂型胶黏剂和压敏胶黏剂的增黏树脂，具有优良的初黏性和耐久性。但是传统制备氢化松香季戊四醇酯都是先氢化后酯化，颜色较深，稳定性不理想，成本高，不能满足高端应用要求。
技术实现思路
本专利技术的目的在于提供一种氢化松香季戊四醇酯的制备方法，这种方法制备的氢化松香季戊四醇酯颜色白，合成成本低。为了实现上述目的，本专利技术采用的技术方案如下：一种氢...
【技术保护点】
一种氢化松香季戊四醇酯制备方法，其特征在于：包括以下步骤：将松香季戊四醇酯和松节油加入到反应釜中，加入催化剂，植物油，通入氢气，氢气压力为5‑35兆帕，升温至80‑300度，反应1‑10小时，加压除去溶剂得到氢化松香季戊四醇酯。
【技术特征摘要】
1.一种氢化松香季戊四醇酯制备方法，其特征在于：包括以下步骤：将松香季戊四醇酯和松节油加入到反应釜中，加入催化剂，植物油，通入氢气，氢气压力为5-35兆帕，升温至80-300度，反应1-10小时，加压除去溶剂得到氢化松香季戊四醇酯。2.根据权利要求1所述的氢化松香季戊四醇酯的制备方法，其特征在于：所述的催化剂为钯碳、钯三氧化铝、合金镍中的一种。3.根据权利要求1或2所述的氢化松香季戊四醇酯的制备方法，其特征在于：所述的松香季戊四醇酯、松节油、植物油和催化剂的质量比1:1～5:0.05～0.3:0.01～0.1。4.根据权利...
【专利技术属性】
技术研发人员：李军，申利群，雷福厚，李玉明，黄志恒，白春星，张鹏程，
申请(专利权)人：广西鼎弘树脂有限公司，
类型：发明
国别省市：广西,45