The invention discloses a waste rubber regenerating agent and its preparing method, including softening agent and activator, which according to the weight, the softener comprises the following ingredients: tall oil, pine tar, paraffin oil and rosin; activating agent comprises the following components: toluene, acetic acid, zinc chloride and tannic acid; the invention of softener the collision and activator by spraying mixed mode, at the same time in the mixing process in nitrogen or argon as the plasma modification of protective gas, after regeneration liquid plasma modification in ultrasonic environment static 1 4H; the invention by plasma modification and ultrasonic vibration prevention large clusters of regeneration agent, increase the contact area and waste rubber regeneration agent, so as to improve the reaction rate and the quality of the.
【技术实现步骤摘要】
一种废橡胶再生剂及其制备方法
本专利技术涉及废旧橡胶回收利用
，具体涉及一种废橡胶再生剂及其制备方法。
技术介绍
随着我国经济的不断发展，橡胶各种橡胶制品在国内市场得到了越来越广泛的应用，但是其在给生活带来极大的便利的同时也带来了巨大的环保压力，而废旧橡胶制品的回收利用又以废旧轮胎的回收处理的环保压力最大；废旧轮胎是有毒、具有较强抗热性和抗降解性的固体废弃物，其自然降解过程长达数百年，因此，解决废旧轮胎的回收再利用问题对于改善生存环境具有重要意义。废旧橡胶的再生是指利用物理、化学或者生物方法破坏橡胶的交联网络，形成线性化的、可再加工的橡胶原材料的过程；目前国内应用较多的再生胶制备手段是高温高压动态脱硫法，其生产流程是将废橡胶、软化剂、脱硫剂等投入到高温高压罐中，在2-4MPa、210℃-300℃的环境中保温3-5小时得到脱硫废胶粉，然后经精炼得到片状再生胶。该工艺过程虽然能够制备品质较好的再生胶，但是其存在能耗大、产生大量废水、废气等重污染物的缺陷。公开号为CN1325917A的中国专利技术专利公开了一种废胶橡胶再生方法，该专利技术将废旧橡胶的粗切颗粒用苯类...
【技术保护点】
一种废橡胶再生剂，其特征在于：包括如下按照重量份数计的组分，98%‑85%的活化剂；2%‑15%的软化剂；所述活化剂包括按重量份数计的以下组分甲苯15‑20份、乙酸2‑4份、氯化锌1‑3份和丹宁酸0.5‑1.5份；所述软化剂包括按重量份数计的以下组分妥尔油20‑35份、松焦油8‑15份、石蜡油5‑10份和松香1‑4份。
【技术特征摘要】
1.一种废橡胶再生剂，其特征在于：包括如下按照重量份数计的组分，98%-85%的活化剂；2%-15%的软化剂；所述活化剂包括按重量份数计的以下组分甲苯15-20份、乙酸2-4份、氯化锌1-3份和丹宁酸0.5-1.5份；所述软化剂包括按重量份数计的以下组分妥尔油20-35份、松焦油8-15份、石蜡油5-10份和松香1-4份。2.根据权利要求1所述的一种废橡胶再生剂的制备方法，其特征在于包括以下步骤：a、将甲苯、乙酸、氯化锌和丹宁酸均匀混合制备活化剂溶液；b、将妥尔油、松焦油、石蜡油、松香均匀混合制备软化剂；c、将软化剂和活化剂通过高压喷头，使软化剂和活化剂雾化碰撞混合，同时向反应器中通入保护气，并接通等离子放电装置进行等离子改性处理得到再生剂原液；d、将再生剂原液置于超声波环境中静置1-4h，得到废...
【专利技术属性】
技术研发人员：陈伟，冯再，
申请(专利权)人：成都新火环保科技有限公司，
类型：发明
国别省市：四川,51