一种以炭材料为催化剂制备氢气和纤维碳的方法技术
Method for preparing hydrogen and carbon fiber by using carbon material as catalyst
The invention relates to a method for preparing hydrogen and carbon fiber by using carbon material as catalyst, belonging to the technical field of catalyst. A method for catalyst preparation of hydrogen and carbon fiber in carbon materials, which is characterized in that: the method of mixed gas containing methane and hydrogen as raw materials, using carbon materials as catalyst, to 600 to 1200 DEG C, the reaction under atmospheric pressure, the hydrogen gas mixture accounted for 1% of total traffic to 90%. This method can effectively improve the stability of methane catalytic decomposition of carbon materials, and carbon fiber, has important application value for carbon catalytic methane decomposition to hydrogen and carbon materials and industrial applications to enhance the decomposition of methane carbon deposition generating economic benefits.
【技术实现步骤摘要】
一种以炭材料为催化剂制备氢气和纤维碳的方法
本专利技术涉及一种以炭材料为催化剂制备氢气和纤维碳的方法，属于催化剂
技术介绍
随着燃料电池的发展和应用，制备不含CO2或者CO的高纯氢气成为一大需求。催化甲烷裂解制取高氢气因其过程简单、产物只有氢气和固态碳两种而易于分离等优点，具有广阔的前景。与金属催化剂相比，炭材料催化剂虽然所需反应温度较高，但具有原料来源广、价格低廉、抗硫等有害杂质及耐高温等诸多优势，因而在甲烷催化裂解制氢过程中受到广泛关注。炭材料催化剂具有较高的初始活性，但稳定性相对较差，而且裂解生成的碳通常为无定型碳，一定程度上制约其应用。
技术实现思路
基于上述理论和认识，本专利技术提供了一种既提高炭催化甲烷裂解制氢催化剂的稳定性、又富产纤维碳的新方法。一种以炭材料为催化剂制备氢气和纤维碳的方法，所述方法以含有甲烷与氢气的混合气为原料，以炭材料为催化剂，于600～1200℃、常压下反应，其中，氢气占混合气总流量的1％～90％。上述技术方案是以含甲烷与氢气的混合气为原料，以炭材料为催化剂，于600～1200℃常压下反应，获得产物为氢气和纤维碳。上述技术方...
【技术保护点】
一种以炭材料为催化剂制备氢气和纤维碳的方法，其特征在于：所述方法以含有甲烷和氢气的混合气为原料，以炭材料为催化剂，于600～1200℃、常压下反应，其中，氢气占混合气总流量的1％～90％。
【技术特征摘要】
1.一种以炭材料为催化剂制备氢气和纤维碳的方法，其特征在于：所述方法以含有甲烷和氢气的混合气为原料，以炭材料为催化剂，于600～1200℃、常压下反应，其中，氢气占混合气总流量的1％～90％。2.根据权利要求1所述的方法，其特征在于：所述混合气的空速为1～100L/(h·gcat)。3.根据权利要求1所述的方法，其特征在于：所述氢气占混合气总流量的5％～50％。4.根据权利要求3所述的方法，其特征在于：所述氢气...
【专利技术属性】
技术研发人员：靳立军，胡浩权，王焦飞，李扬，
申请(专利权)人：大连理工大学，
类型：发明
国别省市：辽宁,21