The invention discloses a method for preparing environmentally sound insulation board and sound insulation layer, the environmental noise from the surface, base plate, the base includes at least two insulation layer; the insulating layer is arranged on the surface of the sound absorption hole groove has a conical, sound insulation layer is arranged between the thickness of polyethylene foam material 0.5 1 cm the. The invention also provides a method for preparing a sound insulation layer, the method comprises the following steps: the component into a high pressure homogenizer, at 21.5 22MPa, 65 70 C 10 stirring for 20 minutes, pressing, get the sound insulation layer.
【技术实现步骤摘要】
一种环保隔音板材及隔音层的制备方法
本专利技术属于隔音材料领域,特别涉及一种环保隔音板材及隔音层的制备方法。
技术介绍
随着城市化进程的不断加速,噪声污染也日益严重,为了保证人们良好的生活和工作环境,有效地隔断噪声,常用的方法是通过水泥和玻璃墙来起到隔绝的作用,但这些材料不仅质量重而且隔音效果不佳,因此难以满足人们隔绝噪声的要求。声音本身是由空气的振动产生的,往往越厚的材料其隔音效果也越好,如何更有效地选择材料来控制噪声音量成为人们关注的问题。
技术实现思路
针对上述的需求,本专利技术特别提供了一种环保隔音板材及隔音层的制备方法。本专利技术的目的可以通过以下技术方案实现:一种环保隔音板材,由表层、基层组成,所述基层包括至少两个隔音层;所述隔音层表面设置有圆锥形的吸声孔槽,隔音层之间设置有厚度为0.5-1厘米的泡沫聚乙烯材料。所述圆锥形的吸声孔槽的底面半径为0.5-1.2厘米。所述圆锥形的吸声孔槽的高为0.3-0.5厘米。所述隔音层的厚度为1.5-2厘米。所述表层为厚度为0.7-2cm的砂浆。所述隔音层由包含以下重量份的组分制成:聚苯乙烯60-75份,聚乙烯20-35份,玻璃纤维5-6份,粉煤灰3-5份,碳酸钙0.5-1.2份,三(2.4-二叔丁基苯基)亚磷酸酯0.8-2份,癸二酸二酰肼0.02-0.2份,二苯甲酮0.2-0.8份。一种隔音层的制备方法,该方法包括以下步骤:(1)称取聚苯乙烯60-75重量份、聚乙烯20-35重量份、玻璃纤维5-6重量份、粉煤灰3-5重量份、碳酸钙0.5-1.2重量份、三(2.4-二叔丁基苯基)亚磷酸酯0.8-2重量份、癸二酸二酰 ...
【技术保护点】
一种环保隔音板材,其特征在于,由表层、基层组成,所述基层包括至少两个隔音层;所述隔音层表面设置有圆锥形的吸声孔槽,隔音层之间设置有厚度为0.5‑1厘米的泡沫聚乙烯材料。
【技术特征摘要】
1.一种环保隔音板材,其特征在于,由表层、基层组成,所述基层包括至少两个隔音层;所述隔音层表面设置有圆锥形的吸声孔槽,隔音层之间设置有厚度为0.5-1厘米的泡沫聚乙烯材料。2.根据权利要求1所述的环保隔音板材,其特征在于:所述圆锥形的吸声孔槽的底面半径为0.5-1.2厘米。3.根据权利要求1所述的环保隔音板材,其特征在于:所述圆锥形的吸声孔槽的高为0.3-0.5厘米。4.根据权利要求1所述的环保隔音板材,其特征在于:所述隔音层的厚度为1.5-2厘米。5.根据权利要求1所述的环保隔音板材,其特征在于:所述隔音层由包含以下重量份的组分制成:聚苯乙烯60-75份,聚乙烯20-35份,...