The invention relates to a method for leaching recovered cobalt, iron and lithium in the cathode material of lithium cobalt phosphate and lithium iron phosphate, belonging to the recycling field of waste materials. In order to reduce the waste battery cathode material of lithium cobalt recovery costs are too high, and low purity technology, the present invention provides a failure of lithium cobalt oxide and lithium iron phosphate cathode material, lithium cobalt and iron combined recovery method, the method of using oxidation in acid solution between two kinds of cathode materials for lithium batteries have joint the leaching reduction reaction, this method eliminates the need for a separate leaching for oxidizing or reducing agent, low cost, simple operation, and recovery of cobalt and lithium were greater than 99.2%, iron phosphate precipitation rate can reach more than 99.5%.
【技术实现步骤摘要】
一种失效钴酸锂和磷酸铁锂正极材料中浸取回收钴、铁、锂的方法
本专利技术涉及一种失效钴酸锂和磷酸铁锂正极材料中浸取回收钴、铁、锂的方法，属于废旧材料回收领域。
技术介绍
在失效钴酸锂电池正极材料有价元素的回收方面的研究中多为在酸性体系加入还原剂浸出钴、锂；在失效磷酸铁锂电池正极材料有价元素的回收方面的研究中多为酸性体系加入氧化剂浸出锂，同时沉淀磷酸铁。关于从失效钴酸锂电池正极材料中回收钴、锂的方法，现有技术多为在酸性体系中加入还原剂(如双氧水、Na2SO3)浸出钴、锂。在国外，SONY等公司已提出了从废旧锂离子二次电池中回收钴化合物的方案。此外，一些研究者也进行了相关的研究：Zhang等采用萃取、沉淀的方法回收了碳酸锂和草酸钴；Contestabile等还综合回收了废旧锂离子二次电池的不锈钢外壳及铝、铜等集流极.在国内尚未有公司提出自己的废旧锂离子二次电池回收方案，这些回收方案的目的主要是回收钴化合物或钴金属单质。《废旧锂离子电池正极材料钴酸锂的回收》采用不同的回收方案对废旧锂离子二次电池进行了回收研究：采用碳酸丙烯酯(PC)回收电解质；采用N‐甲基吡咯烷酮(NMP...
【技术保护点】
一种失效钴酸锂和磷酸铁锂正极材料中浸取回收钴、铁、锂的方法，该方法具体包括如下步骤：(1)将失效钴酸锂正极材料和失效磷酸铁锂正极材料按照钴铁元素摩尔比1：1的比例混合，得到混合材料；向混合材料中加水调浆并持续搅拌，得到浆体；向浆体中缓慢加入无机酸，在25℃～90℃持续反应0.5～6小时，得到反应液；(2)向反应液中滴加无机碱溶液，调节其pH值至2.0～4.0；(3)过滤进行液固分离。
【技术特征摘要】
1.一种失效钴酸锂和磷酸铁锂正极材料中浸取回收钴、铁、锂的方法，该方法具体包括如下步骤：(1)将失效钴酸锂正极材料和失效磷酸铁锂正极材料按照钴铁元素摩尔比1：1的比例混合，得到混合材料；向混合材料中加水调浆并持续搅拌，得到浆体；向浆体中缓慢加入无机酸，在25℃～90℃持续反应0.5～6小时，得到反应液；(2)向反应液中滴加无机碱溶液，调节其pH值至2.0～4.0；(3)过滤进行液固分离。2.根据权利要求1所述的一种失效钴酸锂和磷酸铁锂正极材料中浸取回收钴、铁、锂的方法中，其特征在于，所述的...