一种防水微孔膜的制备方法技术

本发明专利技术公开了一种防水微孔膜的制备方法，包括：(1)将聚乙二醇和聚四氢呋喃醚混合后脱水，控制温度在75‑85℃，加入4,4’二苯基甲烷二异氰酸酯，恒温至少30min；(2)加入1,4‑丁二醇作为扩链剂，加入辛酸亚锡，搅拌，温度达到120℃后，成膜，得到所述防水微孔膜。本发明专利技术合成的聚氨酯的溶血率均小于5％，符合生物材料的溶血性要求，同时材料的抗血小板粘附性能也很好。

Method for preparing waterproof microporous membrane

The invention discloses a method for preparing a waterproof, microporous membrane, including: (1) polyethylene glycol and polytetramethylene ether mixture after dehydration, temperature control in 75 85 DEG C, adding 4,4 'two phenyl methane diisocyanate, temperature of at least 30min; (2) adding 1,4 butylene glycol as chain extender, adding acid stannous, stirring, film-forming temperature reaches 120 DEG C, and get the waterproof membrane. The synthetic polyurethane has a hemolysis rate of less than 5%, conforms to the hemolytic requirements of biological materials, and has good anti platelet adhesion property.

【技术实现步骤摘要】
一种防水微孔膜的制备方法
本专利技术涉及材料
，尤其涉及一种防水微孔膜的制备方法。
技术介绍
防水可呼吸性是指聚合物薄膜及涂层不允许水滴透过，同时却要保证水蒸汽分子自由透过，达到防水可呼吸的目的。这类材料生产的衣物，鞋袜等既可起到防水的作用，又避免了传统的恶劣环境用衣物产生的闷热，冷湿等不适的缺点。根据防水可呼吸的原理不同，该材料可分为三类：微孔型、亲水型和形状记忆型。微孔型是通过控制孔径的大小来达到防水可呼吸的目的：亲水型是无孔膜，主要通过材料中的亲水基团对水蒸汽分子的吸附-扩散达到防水可呼吸的目的：形状记忆型是通过控制聚合物材料的玻璃化转变温度来达到相同的目的。后两种为无孔结构可起到防菌的作用，同样微孔型通过控制微孔的大小也可起到防菌的效果，因此这类功能型材料在医疗方面的应用也越来越广，可用于伤口敷料、外科手术服及保护性衣物、医用手套等。
技术实现思路
本专利技术的目的在于提出一种防水微孔膜的制备方法，其防水透气性良好。为达此目的，本专利技术采用以下技术方案：一种防水微孔膜的制备方法，包括：(1)将聚乙二醇和聚四氢呋喃醚混合后脱水，控制温度在75-85℃，加入4,4’二苯基甲烷本文档来自技高网...

【技术保护点】
一种防水微孔膜的制备方法，包括：(1)将聚乙二醇和聚四氢呋喃醚混合后脱水，控制温度在75‑85℃，加入4,4’二苯基甲烷二异氰酸酯，恒温至少30min；(2)加入1,4‑丁二醇作为扩链剂，加入辛酸亚锡，搅拌，温度达到120℃后，成膜，得到所述防水微孔膜。

【技术特征摘要】
1.一种防水微孔膜的制备方法，包括：(1)将聚乙二醇和聚四氢呋喃醚混合后脱水，控制温度在75-85℃，加入4,4’二苯基甲烷二异...