With light cured polyimide film and method for a flexible or thin film solar cell preparation method comprises the following components: the weight of polyimide nano aluminum 0.1 100; 0.0001; light curing agent 0.5~1.25; antioxidant 0.1~0.2; ultraviolet absorbent 0.1~0.2; amine light stabilizer 0.1~0.2. The use of screw extrusion equipment, polyimide blend; nanometer aluminum powder; curing agent; antioxidant; hindered amine light stabilizer blends, and filtered into the extrusion die casting, cooling, drawing and coiling process obtained by light cured polyimide film solar cell. The product produced by the invention is attached to the surface of the solar cell or the upper encapsulation film of the solar cell, and directly improves the power generation efficiency of the flexible or thin-film solar cells.
【技术实现步骤摘要】
薄膜太阳能电池用光固化聚酰亚胺膜及其制备方法
本专利技术涉及一种柔性或薄膜太阳能电池用光固化聚酰亚胺膜及其制备方法，通过使用该膜封装在柔性或薄膜太阳能电池入光面的表面，直接提高柔性或薄膜太阳能电池的效率。
技术介绍
在太阳能的有效利用项目当中：光电利用是近些年来发展最快，最具活力的研究领域。一般太阳能电池的制作主要是以半导体材料为基础，利用光电材料吸收光能后发生光电转换反应发电。根据所用材料的不同，太阳能电池可分为：1、硅太阳能电池；2、以无机盐如砷化镓III-V化合物、硫化镉、铜铟硒等多元化合物为材料的太阳能电池；3、以功能高分子材料制备的太阳能电池；4、纳米晶太阳能电池等。现有技术工作效率最高的是以III-V族半导体无机材料为原材料的产品。例如:砷化镓/锗单一接面型的量子井陷晶结构，其光电转换效率可达>18%；而多重接面量子井陷晶结构之太阳电池，例如:磷化铟镓/砷化镓/锗，其光电转换效率可高达>30%。目前应用最广，以硅为主：包括非晶硅，光电转换效率约9%；多晶硅，光电转换效率约14%；单晶硅，光电转换效率约17%。虽然在价格上，VI族元素Si要比...
【技术保护点】
一种薄膜太阳能电池用光固化聚酰亚胺膜，其特征在于，包括下述重量份的如下组分：聚酰亚胺100；纳米铝粉0.0001‑0.1；光固化剂0.5~1.25；抗氧剂0.1~0.2；紫外吸收剂0.1~0.2；胺类光稳定剂0.1~0.2；所述的聚酰亚胺树脂为经引入含氟、硅、磷的基团或羟基，或引入脂肪结构单元或采用能使主链弯曲的单体改性的聚酰亚胺树脂。
【技术特征摘要】
1.一种薄膜太阳能电池用光固化聚酰亚胺膜，其特征在于，包括下述重量份的如下组分：聚酰亚胺100；纳米铝粉0.0001-0.1；光固化剂0.5~1.25；抗氧剂0.1~0.2；紫外吸收剂0.1~0.2；胺类光稳定剂0.1~0.2；所述的聚酰亚胺树脂为经引入含氟、硅、磷的基团或羟基，或引入脂肪结构单元或采用能使主链弯曲的单体改性的聚酰亚胺树脂。2.根据权利要求1所述的薄膜太阳能电池用光固化聚酰亚胺膜，其特征在于：所述的胺类光稳定剂为双（1-辛氧基-2,2,6,6-四甲基-4-哌啶基）癸二酯或（2,2,6,6-四甲基-4-哌啶基）癸二酸酯，聚丁二酸（4-羟基-2,2,6,6-四甲基-1哌啶乙醇酯）中的一种或几种的混合。3.根据权利要求1所述的薄膜太阳能电池用光固化聚酰亚胺膜，其特征在于：所述的光固化剂为芳香族羰基化合物。4.根据权利要求1所述的薄膜太阳能...